- 密度 [g/cm3]: 1.76
- 弯曲模量 [MPa]: 0.200
- 脆化温度 [℃]: -53.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 15 g/10 min @Load 5.00 kg, Temperature 230 °C | 15 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 475 % | 475 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 0.200 GPa | 29.0 ksi | 2mm/min; ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | 10 mA, after 2 min; ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+14 ohm | >= 1.00e+14 ohm | < 1V after 2 min - 500 V; ASTM D257 | ||
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 168 °C | 334 °F | ASTM D3418 | ||
| Brittleness Temperature | -53.0 °C | -63.4 °F | ASTM D746A | ||
| Oxygen Index | >= 65 % @Thickness 3.00 mm | >= 65 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.