- 密度 [g/cm3]: 1.77
- 拉伸强度 [MPa]: 38.0
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Linear Mold Shrinkage | 0.030 cm/cm | 0.030 in/in | |||
| Melt Index of Compound | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 3.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 3.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 225 % | 225 % | 50mm/min; ASTM D638 | ||
| Elongation at Yield | 11 % | 11 % | 50mm/min; ASTM D638 | ||
| Tensile Modulus | 1.30000 GPa | 188.549 ksi | 1mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 173 °C | 343 °F | ASTM D3418 | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |||
| Descriptive Properties | |||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.