- 密度 [g/cm3]: 1.78
- 缺口冲击强度: 1.6
- 断裂伸长率 [%]: 74.1
- 弯曲强度 [MPa]: 53.4
- 弯曲模量 [MPa]: 2.30
- 硬度: 100.0
- 热变形温度 [℃]: 149.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Ultimate | 53.4 MPa | 7750 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Modulus of Elasticity | 2.40 GPa | 348 ksi | 1% Secant; ASTM D638 |
| Flexural Yield Strength | 74.1 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | Tangent; ASTM D790 |
| Compressive Yield Strength | 80.0 MPa | 11600 psi | ASTM D695 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+14 ohm-cm | 5.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 9.0 @Frequency 60 Hz | 9.0 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 11.0 kV/mm | 280 kV/in | ASTM D149 |
| Dissipation Factor | 0.060 @Frequency 60 Hz | 0.060 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 128 µm/m-°C @Temperature 20.0 °C | 71.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 178 °C | 352 °F | ASTM D3448 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |