- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.78
- 缺口冲击强度: 1.8
- 拉伸强度 [MPa]: 15.0
- 弯曲强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 0.360
- 热变形温度 [℃]: 62.0
- 脆化温度 [℃]: -22.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.040 % | <= 0.040 % | ISO 62 (method 1) |
| Linear Mold Shrinkage | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 @Thickness 2.00 mm | 60 @Thickness 0.0787 in | ASTM D2240 |
| Tensile Strength, Ultimate | 30.0 - 50.0 MPa | 4350 - 7250 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 15.0 - 18.0 MPa | 2180 - 2610 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 600 - 750 % | 600 - 750 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 12 - 15 % | 12 - 15 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 0.360 - 0.480 GPa | 52.2 - 69.6 ksi | 1 mm/min; ASTM D638 |
| Flexural Modulus | 0.360 - 0.440 GPa | 52.2 - 63.8 ksi | 2 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.80 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 3.37 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 15 | 5.0 - 15 | CS10 / 1 kg |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 23.0 J/g | 9.89 BTU/lb | 80°C to end of melting |
| 24.0 J/g | 10.3 BTU/lb | Crystallization Heat | |
| CTE, linear | 150 - 180 µm/m-°C @Temperature 20.0 °C | 83.3 - 100 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 135 °C | 275 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 92.0 °C | 198 °F | |
| Maximum Service Temperature, Air | 340 - 375 °C | 644 - 707 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C @Thickness 4.00 mm | 144 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C @Thickness 4.00 mm | 104 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Vicat Softening Point | 120 °C @Load 1.00 kg, Thickness 4.00 mm | 248 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| Brittleness Temperature | -22.0 °C | -7.60 °F | ASTM D746A |
| Glass Transition Temp, Tg | -29.0 °C | -20.2 °F | DMTA |
| Oxygen Index | 44 - 65 % @Thickness 3.00 mm | 44 - 65 % @Thickness 0.118 in | sheet; ASTM D2863 |