Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product

Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product 物性表: Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product 物性表及特性介绍,Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product 注塑参数详情,如需Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product 下载, 可到相关下载区下载
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 0.267
  • 断裂伸长率 [%]: 17.2
  • 弯曲模量 [MPa]: 2.07
  • 硬度: 80.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.91 g/cc1.91 g/ccASTM D792
Water Absorption 0.1 %0.1 %Immersion, 24hr; ASTM D570(2)
Water Absorption at Saturation 0.3 %0.3 %Immersion; ASTM D570(2)
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 8080ASTM D785
Hardness, Shore D 7474ASTM D2240
Tensile Strength 8.96 MPa1300 psiASTM D638
Elongation at Break 3.0 %3.0 %ASTM D638
Tensile Modulus 2.55 GPa370 ksiASTM D638
Flexural Yield Strength 17.2 MPa2500 psiASTM D790
Flexural Modulus 2.07 GPa300 ksiASTM D790
Compressive Strength 48.3 MPa7000 psi10% Def.; ASTM D695
Compressive Modulus 1.38 GPa200 ksiASTM D695
Shear Strength 11.7 MPa1700 psiASTM D732
Izod Impact, Notched 0.267 J/cm0.500 ft-lb/inASTM D256 Type A
Coefficient of Friction, Dynamic <= 0.15<= 0.15Dry vs. Steel; 20 fpm/250 psi; QTM55007
Coefficient of Friction, Static <= 0.20<= 0.2050 lb load, 90° rotation; QTM55007
K (wear) Factor 64.5 x 10-8 mm³/N-M32.0 x 10-10 in³-min/ft-lb-hrQTM 55010
Limiting Pressure Velocity 0.501 MPa-m/sec14300 psi-ft/min4:1 safety factor; QTM 55007
 
Electrical PropertiesMetricEnglishComments
Surface Resistivity per Square <= 100000 ohm<= 100000 ohmEOS/ESD S11.11
 
Thermal PropertiesMetricEnglishComments
CTE, linear 45.0 µm/m-°C
@Temperature -40.0 - 149 °C
25.0 µin/in-°F
@Temperature -40.0 - 300 °F
ASTM E831
Melting Point 327 °C621 °FCrystalline, Peak; ASTM D3418
Maximum Service Temperature, Air 260 °C500 °FLong Term
Deflection Temperature at 1.8 MPa (264 psi) 104 °C220 °FASTM D648
Flammability, UL94 V-0V-01/8 inch (Estimated Rating)
 
Chemical Resistance PropertiesMetricEnglishComments
Acids, Strong (pH 1-3) AcceptableAcceptable
Acids, Weak AcceptableAcceptable
Alcohols AcceptableAcceptable
Alkalies, Strong (pH 11-14) UnacceptableUnacceptable
Alkalies, Weak AcceptableAcceptable
Chlorinated Solvents AcceptableAcceptable
Conductive / Static Dissipative YesYes
Continuous Sunlight AcceptableAcceptable
Ethers AcceptableAcceptable
Hydrocarbons - Aliphatic AcceptableAcceptable
Hydrocarbons - Aromatic AcceptableAcceptable
Inorganic Salt Solutions AcceptableAcceptable
Ketones, Esters AcceptableAcceptable

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-43566.html

免责声明: 本文 Quadrant EPP Fluorosint® 135 PTFE and PPS Blend, with Proprietary Lubrication Fillers (ASTM Product 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络