- 密度 [g/cm3]: 2.26
- 吸水率 [%]: 0.02
- 弯曲模量 [MPa]: 3.01
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.26 g/cc | 0.0816 lb/in³ | ASTM D792 Method A | ||
| Water Absorption | 0.020 % | 0.020 % | IPC TM-650 2.6.2.2 | ||
| Outgassing - Total Mass Loss | 0.00 % @Pressure <=1.33e-10 MPa, Temperature 125 °C | 0.00 % @Pressure <=1.93e-8 psi, Temperature 257 °F | Collected Volatiles; NASA SP-R-0022A | ||
| 0.010 % @Pressure <=1.33e-10 MPa, Temperature 125 °C | 0.010 % @Pressure <=1.93e-8 psi, Temperature 257 °F | Water Vapor Recovered; NASA SP-R-0022A | |||
| 0.020 % @Pressure <=1.33e-10 MPa, Temperature 125 °C | 0.020 % @Pressure <=1.93e-8 psi, Temperature 257 °F | NASA SP-R-0022A | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 77.2 MPa | 11200 psi | Cross; ASTM D882 | ||
| 103 MPa | 14900 psi | Machine; ASTM D882 | |||
| Modulus of Elasticity | 2.39 GPa | 346 ksi | Cross; ASTM D638 | ||
| 3.34 GPa | 485 ksi | Machine; ASTM D638 | |||
| Flexural Modulus | >= 3.01 GPa | >= 437 ksi | ASTM D790 | ||
| Compressive Modulus | 2.25 GPa | 327 ksi | ASTM D695 | ||
| Peel Strength | 2.45 kN/m | 14.0 pli | After Thermal Stress; IPC TM-650 2.4.8 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.50e+15 ohm-cm | 1.50e+15 ohm-cm | C96/35/90; IPC TM-650 2.5.17.1 | ||
| Surface Resistance | 3.40e+13 ohm | 3.40e+13 ohm | C96/35/90; IPC TM-650 2.5.17.1 | ||
| Dielectric Constant | 2.33 @Frequency 1.00e+6 Hz | 2.33 @Frequency 1.00e+6 Hz | C23/50; IPC TM-650 2.5.5.3 | ||
| 2.33 @Frequency 1.00e+10 Hz | 2.33 @Frequency 1.00e+10 Hz | C23/50; IPC TM-650 2.5.5.5 | |||
| Dielectric Breakdown | >= 45000 V | >= 45000 V | D48/50; ASTM D149 | ||
| Dissipation Factor | 0.00090 @Frequency 1.00e+6 Hz | 0.00090 @Frequency 1.00e+6 Hz | C23/50; IPC TM-650 2.5.5.3 | ||
| 0.0013 @Frequency 1.00e+10 Hz | 0.0013 @Frequency 1.00e+10 Hz | C23/50; IPC TM-650 2.5.5.5 | |||
| Arc Resistance | >= 180 sec | >= 180 sec | D48/50; ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 17.0 µm/m-°C @Temperature 0.000 - 100 °C | 9.44 µin/in-°F @Temperature 32.0 - 212 °F | x direction; IPC TM-650 2.4.24 | ||
| 29.0 µm/m-°C @Temperature 0.000 - 100 °C | 16.1 µin/in-°F @Temperature 32.0 - 212 °F | y direction; IPC TM-650 2.4.24 | |||
| CTE, linear, Transverse to Flow | 217 µm/m-°C @Temperature 0.000 - 100 °C | 121 µin/in-°F @Temperature 32.0 - 212 °F | z direction; IPC TM-650 2.4.24 | ||
| Thermal Conductivity | 0.257 W/m-K @Temperature 100 °C | 1.78 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1225 | ||
| Flammability, UL94 | V-0 | V-0 | Vertical Burn | ||
| Descriptive Properties | |||||
| Temperature Coefficient of Dielectric (ppm/°C) | -161 | IPC TM-650 2.5.5.5 (-10 - 140°C) | |||