- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 4.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.5 % | 4.5 % | ISO 62 | ||
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 290 MPa | 42100 psi | conditioned; ISO 2039-1 | ||
| 300 MPa | 43500 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 265 MPa | 38400 psi | conditioned; ISO 527-1/-2 | ||
| 275 MPa | 39900 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 | ||
| 2.0 % | 2.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 24.0 GPa | 3480 ksi | conditioned; ISO 527-1/-2 | ||
| 24.5 GPa | 3550 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | dry; ISO 179/1eU | ||
| 5.50 J/cm² | 26.2 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature 30.0 °C | 23.8 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature 30.0 °C | 23.8 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.800 J/cm² | 3.81 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5000 ohm-cm | 5000 ohm-cm | dry; IEC 60093 | ||
| 5000 ohm-cm | 5000 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 100 ohm | 100 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 310 °C | 590 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | long term; EMS | ||
| 240 °C | 464 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Compressed air systems | ||||
| Fuel systems | |||||
| Hydraulic systems | |||||
| Interior | |||||
| Powertrain and Chassis | |||||
| Electricals & Electronics | Electrical equipment | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Hydraulics & Pneumatics | |||||
| Mechanical Engineering | |||||
| Power transmission | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Co Polyamide | ||||
| Improved alcohol resistance | |||||
| Improved friction & wear properties | |||||
| Partially aromatic Polyamide | |||||
| Special Characteristics | Anti-static | ||||
| Improved heat resistance | |||||