- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 7.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 100 MPa | 14500 psi | conditioned; ISO 2039-1 | ||
| 200 MPa | 29000 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | conditioned; ISO 527-1/-2 | ||
| 155 MPa | 22500 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 10 % | 10 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 5.70 GPa | 827 ksi | conditioned; ISO 527-1/-2 | ||
| 8.50 GPa | 1230 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | dry; ISO 179/1eU | ||
| 7.50 J/cm² | 35.7 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 4.50 J/cm² @Temperature 30.0 °C | 21.4 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 4.50 J/cm² @Temperature 30.0 °C | 21.4 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.30 J/cm² | 6.19 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | conditioned; IEC 60243-1 | ||
| 24.0 kV/mm | 610 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 425 V | 425 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS | ||
| 180 °C | 356 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Interior | ||||
| Electricals & Electronics | Electrical appliances | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Mechanical Engineering | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||