- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 117
- 弯曲模量 [MPa]: 3.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | Immersion, 24hr; ASTM D570 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 97 | 97 | ASTM D785 |
| Tensile Strength | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 2.24 GPa | 325 ksi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| K (wear) Factor | 201 x 10-8 mm³/N-M | 100 x 10-10 in³-min/ft-lb-hr | QTM 55100 |
| Limiting Pressure Velocity | 0.0946 MPa-m/sec | 2700 psi-ft/min | QTM 55007 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature -40.0 - 150 °C | 50.0 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E831 |
| Thermal Conductivity | 0.303 W/m-K | 2.10 BTU-in/hr-ft²-°F | |
| Melting Point | 290 °C | 554 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 149 °C | 300 °F | Continuous |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Compliance Properties | Metric | English | Comments |
| 3A-Dairy | No | No | |
| Canada AG | No | No | |
| FDA | No | No | |
| NSF | No | No | |
| USDA | No | No | |
| USP Class VI | No | No | |
| Chemical Resistance Properties | Metric | English | Comments |
| Acids, Strong (pH 1-3) | Unacceptable | Unacceptable | |
| Acids, Weak | Limited | Limited | |
| Alcohols | Limited | Limited | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Limited | Limited | |
| Chlorinated Solvents | Limited | Limited | |
| Conductive / Static Dissipative | No | No | |
| Continuous Sunlight | Limited | Limited | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable | |