- 密度 [g/cm3]: 1.52
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH / 23°C; Similar to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C | 33.3 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B |
| Flammability, UL94 | V-0 @Thickness 0.900 mm | V-0 @Thickness 0.0354 in | |