- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 0.45
- 缺口冲击强度: 0.37
- 拉伸强度 [MPa]: 105.0
- 断裂伸长率 [%]: 110
- 弯曲强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 3.59
- 硬度: 110.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 1.45 g/cc | 0.0397 - 0.0524 lb/in³ | Average value: 1.24 g/cc Grade Count:50 |
| Filler Content | 5.00 - 10.0 % | 5.00 - 10.0 % | Average value: 8.75 % Grade Count:4 |
| Water Absorption | 0.450 - 2.50 % | 0.450 - 2.50 % | Average value: 1.00 % Grade Count:42 |
| Moisture Absorption at Equilibrium | 2.20 - 2.70 % | 2.20 - 2.70 % | Average value: 2.47 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.0180 cm/cm | 0.00100 - 0.0180 in/in | Average value: 0.00492 cm/cm Grade Count:48 |
| Linear Mold Shrinkage, Transverse | 0.00900 - 0.0110 cm/cm | 0.00900 - 0.0110 in/in | Average value: 0.00967 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 125 | 110 - 125 | Average value: 114 Grade Count:9 |
| Tensile Strength, Ultimate | 75.0 - 320 MPa | 10900 - 46400 psi | Average value: 180 MPa Grade Count:42 |
| Tensile Strength, Yield | 105 - 162 MPa | 15200 - 23500 psi | Average value: 144 MPa Grade Count:8 |
| Elongation at Break | 1.00 - 6.00 % | 1.00 - 6.00 % | Average value: 3.25 % Grade Count:21 |
| Elongation at Yield | 1.30 - 11.0 % | 1.30 - 11.0 % | Average value: 3.21 % Grade Count:28 |
| Modulus of Elasticity | 4.69 - 34.0 GPa | 680 - 4930 ksi | Average value: 14.0 GPa Grade Count:42 |
| Flexural Yield Strength | 110 - 440 MPa | 16000 - 63800 psi | Average value: 252 MPa Grade Count:45 |
| Flexural Modulus | 3.59 - 29.0 GPa | 520 - 4210 ksi | Average value: 11.7 GPa Grade Count:46 |
| Izod Impact, Notched | 0.370 - 2.03 J/cm | 0.693 - 3.80 ft-lb/in | Average value: 0.938 J/cm Grade Count:17 |
| 0.5339 - 0.5339 J/cm @Temperature -40.0 - -40.0 °C | 1.000 - 1.000 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.534 J/cm Grade Count:1 | |
| 0.5339 - 0.5339 J/cm @Thickness 3.17 - 3.17 mm | 1.000 - 1.000 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 0.534 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 4.27 - 10.1 J/cm | 8.00 - 19.0 ft-lb/in | Average value: 7.18 J/cm Grade Count:11 |
| Charpy Impact Unnotched | 2.20 - 9.50 J/cm² | 10.5 - 45.2 ft-lb/in² | Average value: 5.15 J/cm² Grade Count:32 |
| 2.20 - 9.00 J/cm² @Temperature -40.0 - -30.0 °C | 10.5 - 42.8 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 4.59 J/cm² Grade Count:16 | |
| Charpy Impact, Notched | 0.400 - 1.50 J/cm² | 1.90 - 7.14 ft-lb/in² | Average value: 0.981 J/cm² Grade Count:24 |
| 0.700 - 1.10 J/cm² @Temperature -30.0 - -30.0 °C | 3.33 - 5.24 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.960 J/cm² Grade Count:5 | |
| Coefficient of Friction | 0.180 - 0.250 | 0.180 - 0.250 | Average value: 0.213 Grade Count:10 |
| Coefficient of Friction, Static | 0.130 - 0.180 | 0.130 - 0.180 | Average value: 0.165 Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+13 ohm-cm | 1.00 - 1.00e+13 ohm-cm | Average value: 2.94e+11 ohm-cm Grade Count:17 |
| Surface Resistance | 1.00 - 1.00e+13 ohm | 1.00 - 1.00e+13 ohm | Average value: 1.71e+11 ohm Grade Count:40 |
| Insulation Resistance | 100 - 1.00e+12 ohm | 100 - 1.00e+12 ohm | Average value: 7.14e+10 ohm Grade Count:28 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.0 - 79.2 µm/m-°C | 6.67 - 44.0 µin/in-°F | Average value: 28.6 µm/m-°C Grade Count:24 |
| Thermal Conductivity | 0.380 - 3.50 W/m-K | 2.64 - 24.3 BTU-in/hr-ft²-°F | Average value: 0.886 W/m-K Grade Count:15 |
| Melting Point | 221 - 262 °C | 430 - 504 °F | Average value: 251 °C Grade Count:7 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 135 °C Grade Count:30 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 260 °C | 410 - 500 °F | Average value: 247 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 - 259 °C | 350 - 498 °F | Average value: 238 °C Grade Count:30 |
| Vicat Softening Point | 200 - 260 °C | 392 - 500 °F | Average value: 248 °C Grade Count:14 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:19 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 289 °C Grade Count:31 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:28 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 299 °C Grade Count:36 |
| Mold Temperature | 65.6 - 121 °C | 150 - 250 °F | Average value: 101 °C Grade Count:39 |
| Drying Temperature | 75.0 - 107 °C | 167 - 225 °F | Average value: 89.4 °C Grade Count:34 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.67 hour Grade Count:3 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:4 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 103 MPa Grade Count:5 |