Overview of materials for Nylon 66, 20% Carbon Fiber Filled

Overview of materials for Nylon 66, 20% Carbon Fiber Filled 物性表: Overview of materials for Nylon 66, 20% Carbon Fiber Filled物性表及特性介绍,Overview of materials for Nylon 66, 20% Carbon Fiber Filled注塑参数详情,如需Overview of materials for Nylon 66, 20% Carbon Fiber Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 0.4
  • 缺口冲击强度: 0.534
  • 拉伸强度 [MPa]: 152.0
  • 断裂伸长率 [%]: 72.4
  • 弯曲强度 [MPa]: 45.5
  • 弯曲模量 [MPa]: 2.07
  • 硬度: 112.0
  • 热变形温度 [℃]: 191.0
 
Physical PropertiesMetricEnglishComments
Density 1.14 - 1.50 g/cc0.0412 - 0.0542 lb/in³Average value: 1.25 g/cc Grade Count:32
Filler Content 15.0 - 20.0 %15.0 - 20.0 %Average value: 18.0 % Grade Count:10
Water Absorption 0.400 - 2.50 %0.400 - 2.50 %Average value: 0.850 % Grade Count:18
Moisture Absorption at Equilibrium 0.400 - 2.50 %0.400 - 2.50 %Average value: 1.86 % Grade Count:5
Water Absorption at Saturation 6.00 - 8.00 %6.00 - 8.00 %Average value: 6.83 % Grade Count:3
Additive Loading 15.0 - 20.0 %15.0 - 20.0 %Average value: 18.3 % Grade Count:3
Linear Mold Shrinkage 0.000500 - 0.0220 cm/cm0.000500 - 0.0220 in/inAverage value: 0.00407 cm/cm Grade Count:30
Linear Mold Shrinkage, 6.35 mm section 0.00250 - 0.0280 cm/cm0.00250 - 0.0280 in/inAverage value: 0.00646 cm/cm Grade Count:7
Linear Mold Shrinkage, Transverse 0.00190 - 0.0110 cm/cm0.00190 - 0.0110 in/inAverage value: 0.00638 cm/cm Grade Count:5
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 112 - 125112 - 125Average value: 118 Grade Count:13
Ball Indentation Hardness 160 - 270 MPa23200 - 39200 psiAverage value: 223 MPa Grade Count:3
Tensile Strength, Ultimate 45.5 - 230 MPa6600 - 33400 psiAverage value: 176 MPa Grade Count:26
Tensile Strength, Yield 152 - 230 MPa22000 - 33400 psiAverage value: 183 MPa Grade Count:6
Elongation at Break 1.00 - 10.0 %1.00 - 10.0 %Average value: 3.10 % Grade Count:31
Modulus of Elasticity 2.21 - 18.6 GPa320 - 2700 ksiAverage value: 13.4 GPa Grade Count:24
Flexural Yield Strength 72.4 - 330 MPa10500 - 47900 psiAverage value: 256 MPa Grade Count:25
Flexural Modulus 2.07 - 16.2 GPa300 - 2350 ksiAverage value: 12.0 GPa Grade Count:28
Compressive Yield Strength 40.0 - 172 MPa5800 - 25000 psiAverage value: 119 MPa Grade Count:4
Izod Impact, Notched 0.534 - 1.92 J/cm1.00 - 3.60 ft-lb/inAverage value: 0.902 J/cm Grade Count:24
Izod Impact, Unnotched 5.34 - 14.9 J/cm10.0 - 28.0 ft-lb/inAverage value: 7.34 J/cm Grade Count:15
Charpy Impact Unnotched 2.60 - 7.20 J/cm²12.4 - 34.3 ft-lb/in²Average value: 4.32 J/cm² Grade Count:7
 2.50 - 4.10 J/cm²
@Temperature -40.0 - -20.0 °C
11.9 - 19.5 ft-lb/in²
@Temperature -40.0 - -4.00 °F
Average value: 3.03 J/cm² Grade Count:3
Charpy Impact, Notched 0.600 - 1.60 J/cm²2.86 - 7.61 ft-lb/in²Average value: 0.906 J/cm² Grade Count:7
 0.400 - 0.500 J/cm²
@Temperature -40.0 - -20.0 °C
1.90 - 2.38 ft-lb/in²
@Temperature -40.0 - -4.00 °F
Average value: 0.450 J/cm² Grade Count:2
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 10.0 - 1.00e+16 ohm-cm10.0 - 1.00e+16 ohm-cmAverage value: 4.17e+14 ohm-cm Grade Count:24
Surface Resistance 20.0 - 1.00e+7 ohm20.0 - 1.00e+7 ohmAverage value: 1.14e+6 ohm Grade Count:11
Dielectric Constant 3.60 - 3.703.60 - 3.70Average value: 3.63 Grade Count:3
Dielectric Strength 2.50 - 20.0 kV/mm63.5 - 508 kV/inAverage value: 15.5 kV/mm Grade Count:4
Dissipation Factor 0.0160 - 0.02000.0160 - 0.0200Average value: 0.0187 Grade Count:3
 
Thermal PropertiesMetricEnglishComments
CTE, linear 18.0 - 72.0 µm/m-°C10.0 - 40.0 µin/in-°FAverage value: 39.5 µm/m-°C Grade Count:14
Thermal Conductivity 0.430 - 0.692 W/m-K2.98 - 4.80 BTU-in/hr-ft²-°FAverage value: 0.537 W/m-K Grade Count:3
Melting Point 221 - 262 °C430 - 504 °FAverage value: 253 °C Grade Count:9
Maximum Service Temperature, Air 115 - 240 °C239 - 464 °FAverage value: 163 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 191 - 260 °C375 - 500 °FAverage value: 248 °C Grade Count:14
Deflection Temperature at 1.8 MPa (264 psi) 64.4 - 259 °C148 - 498 °FAverage value: 241 °C Grade Count:27
Vicat Softening Point 230 - 254 °C446 - 489 °FAverage value: 245 °C Grade Count:3
Flammability, UL94 HB - V-0HB - V-0Grade Count:24
 
Processing PropertiesMetricEnglishComments
Processing Temperature 270 - 300 °C518 - 572 °FAverage value: 284 °C Grade Count:8
Melt Temperature 260 - 300 °C500 - 572 °FAverage value: 286 °C Grade Count:12
Mold Temperature 60.0 - 110 °C140 - 230 °FAverage value: 85.8 °C Grade Count:20
Drying Temperature 79.4 - 100 °C175 - 212 °FAverage value: 80.7 °C Grade Count:11
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourAverage value: 3.71 hour Grade Count:7
Moisture Content 0.150 - 0.200 %0.150 - 0.200 %Average value: 0.194 % Grade Count:9
Dew Point -17.8 °C0.000 °FAverage value: -17.8 °C Grade Count:7
Injection Pressure 68.9 - 124 MPa10000 - 18000 psiAverage value: 102 MPa Grade Count:15

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44767.html

免责声明: 本文 Overview of materials for Nylon 66, 20% Carbon Fiber Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。