- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.29
- 拉伸强度 [MPa]: 34.5
- 断裂伸长率 [%]: 40.0
- 弯曲强度 [MPa]: 3.57
- 弯曲模量 [MPa]: 0.255
- 硬度: 90.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 - 1.67 g/cc | 0.0368 - 0.0603 lb/in³ | Average value: 1.20 g/cc Grade Count:114 |
| Water Absorption | 0.0500 - 9.00 % | 0.0500 - 9.00 % | Average value: 2.10 % Grade Count:79 |
| Moisture Absorption at Equilibrium | 0.170 - 3.10 % | 0.170 - 3.10 % | Average value: 2.11 % Grade Count:23 |
| Water Absorption at Saturation | 7.00 - 9.00 % | 7.00 - 9.00 % | Average value: 8.23 % Grade Count:9 |
| Viscosity Measurement | 140 - 145 | 140 - 145 | Average value: 144 Grade Count:7 |
| Viscosity Test | 150 - 205 cm³/g | 150 - 205 cm³/g | Average value: 178 cm³/g Grade Count:4 |
| Linear Mold Shrinkage | 0.00100 - 0.0250 cm/cm | 0.00100 - 0.0250 in/in | Average value: 0.0132 cm/cm Grade Count:102 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.0119 cm/cm Grade Count:12 |
| Melt Flow | 4.00 - 130 g/10 min | 4.00 - 130 g/10 min | Average value: 49.8 g/10 min Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 - 88.0 | 55.0 - 88.0 | Average value: 77.3 Grade Count:11 |
| Hardness, Rockwell R | 90.0 - 125 | 90.0 - 125 | Average value: 116 Grade Count:40 |
| Ball Indentation Hardness | 120 - 150 MPa | 17400 - 21800 psi | Average value: 135 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 3.57 - 159 MPa | 518 - 23000 psi | Average value: 64.4 MPa Grade Count:63 |
| 24.0 - 116 MPa @Temperature -40.0 - 80.0 °C | 3480 - 16800 psi @Temperature -40.0 - 176 °F | Average value: 37.7 MPa Grade Count:2 | |
| 1.14 - 108.35 MPa @Temperature -40.0 - 100 °C | 165 - 15715 psi @Temperature -40.0 - 212 °F | Average value: 37.7 MPa Grade Count:3 | |
| 1.14 - 108.35 MPa @Strain 0.100 - 50.0 % | 165 - 15715 psi @Strain 0.100 - 50.0 % | Average value: 37.7 MPa Grade Count:3 | |
| Tensile Strength, Yield | 34.5 - 193 MPa | 5000 - 28000 psi | Average value: 73.3 MPa Grade Count:60 |
| 62.0 - 107 MPa @Temperature -40.0 - 77.0 °C | 8990 - 15500 psi @Temperature -40.0 - 171 °F | Average value: 84.5 MPa Grade Count:1 | |
| Elongation at Break | 0.800 - 300 % | 0.800 - 300 % | Average value: 33.9 % Grade Count:96 |
| 20.0 - 300 % @Temperature -40.0 - 77.0 °C | 20.0 - 300 % @Temperature -40.0 - 171 °F | Average value: 160 % Grade Count:1 | |
| Elongation at Yield | 2.00 - 25.0 % | 2.00 - 25.0 % | Average value: 11.5 % Grade Count:34 |
| 5.00 - 30.0 % @Temperature -40.0 - 77.0 °C | 5.00 - 30.0 % @Temperature -40.0 - 171 °F | Average value: 17.5 % Grade Count:1 | |
| Modulus of Elasticity | 1.10 - 14.5 GPa | 160 - 2100 ksi | Average value: 3.42 GPa Grade Count:54 |
| 1.60 - 3.30 GPa @Temperature 40.0 - 100 °C | 232 - 479 ksi @Temperature 104 - 212 °F | Average value: 2.31 GPa Grade Count:1 | |
| Flexural Yield Strength | 40.0 - 276 MPa | 5800 - 40000 psi | Average value: 104 MPa Grade Count:88 |
| 38.0 - 140 MPa @Temperature -40.0 - 80.0 °C | 5510 - 20300 psi @Temperature -40.0 - 176 °F | Average value: 86.8 MPa Grade Count:2 | |
| Flexural Modulus | 0.255 - 12.4 GPa | 37.0 - 1800 ksi | Average value: 3.01 GPa Grade Count:93 |
| 0.400 - 4.30 GPa @Temperature -40.0 - 80.0 °C | 58.0 - 624 ksi @Temperature -40.0 - 176 °F | Average value: 2.14 GPa Grade Count:2 | |
| Compressive Yield Strength | 34.0 - 97.0 MPa | 4930 - 14100 psi | Average value: 79.5 MPa Grade Count:4 |
| Shear Strength | 56.0 - 69.0 MPa | 8120 - 10000 psi | Average value: 63.0 MPa Grade Count:6 |
| Izod Impact, Notched | 0.290 - 7.47 J/cm | 0.543 - 14.0 ft-lb/in | Average value: 0.915 J/cm Grade Count:77 |
| 0.350 - 1.38814 J/cm @Temperature -40.0 - -40.0 °C | 0.656 - 2.60056 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.642 J/cm Grade Count:4 | |
| 0.300 - 0.427 J/cm @Temperature -40.0 - -40.0 °C | 0.562 - 0.800 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.642 J/cm Grade Count:2 | |
| 0.300 - 0.427 J/cm @Thickness 1.57 - 3.17 mm | 0.562 - 0.800 ft-lb/in @Thickness 0.0618 - 0.125 in | Average value: 0.642 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 5.34 J/cm - NB | 10.0 ft-lb/in - NB | Average value: 6.71 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² - NB | 1.43 ft-lb/in² - NB | Average value: 10.3 kJ/m² Grade Count:16 |
| 4.00 - 6.00 kJ/m² @Temperature -30.0 - -30.0 °C | 1.90 - 2.86 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.00 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 45.0 - 60.0 kJ/m² @Temperature -30.0 - -30.0 °C | 21.4 - 28.6 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 53.8 kJ/m² Grade Count:2 |
| Charpy Impact Unnotched | 3.00 J/cm² - NB | 14.3 ft-lb/in² - NB | Average value: 7.05 J/cm² Grade Count:29 |
| 2.00 J/cm² - NB @Temperature -40.0 - -20.0 °C | 9.52 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 5.76 J/cm² Grade Count:13 | |
| Charpy Impact, Notched | 0.150 J/cm² - NB | 0.714 ft-lb/in² - NB | Average value: 0.681 J/cm² Grade Count:29 |
| 0.150 J/cm² - NB @Temperature -40.0 - -20.0 °C | 0.714 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 0.302 J/cm² Grade Count:10 | |
| Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | Average value: 700 MPa Grade Count:3 |
| Taber Abrasion, mg/1000 Cycles | 5.00 - 8.00 | 5.00 - 8.00 | Average value: 7.00 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+18 ohm-cm | 100 - 1.00e+18 ohm-cm | Average value: 4.35e+16 ohm-cm Grade Count:66 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 2.02e+14 ohm Grade Count:32 |
| Dielectric Constant | 2.70 - 8.00 | 2.70 - 8.00 | Average value: 3.88 Grade Count:28 |
| Dielectric Strength | 13.0 - 70.0 kV/mm | 330 - 1780 kV/in | Average value: 26.2 kV/mm Grade Count:45 |
| Dissipation Factor | 0.00500 - 0.200 | 0.00500 - 0.200 | Average value: 0.0443 Grade Count:18 |
| Dielectric Loss Index | 0.0200 - 0.300 | 0.0200 - 0.300 | Average value: 0.128 Grade Count:6 |
| Arc Resistance | 110 - 128 sec | 110 - 128 sec | Average value: 121 sec Grade Count:7 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 578 V Grade Count:39 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.700 - 91.8 µm/m-°C | 0.389 - 51.0 µin/in-°F | Average value: 67.6 µm/m-°C Grade Count:36 |
| Specific Heat Capacity | 1.67 - 1.70 J/g-°C | 0.399 - 0.406 BTU/lb-°F | Average value: 1.69 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.200 - 5.50 W/m-K | 1.39 - 38.2 BTU-in/hr-ft²-°F | Average value: 1.01 W/m-K Grade Count:7 |
| Melting Point | 221 - 275 °C | 430 - 527 °F | Average value: 257 °C Grade Count:67 |
| Maximum Service Temperature, Air | 80.0 - 200 °C | 176 - 392 °F | Average value: 131 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 - 266 °C | 203 - 511 °F | Average value: 212 °C Grade Count:67 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 - 260 °C | 145 - 500 °F | Average value: 88.1 °C Grade Count:98 |
| Vicat Softening Point | 199 - 250 °C | 390 - 482 °F | Average value: 232 °C Grade Count:14 |
| UL RTI, Electrical | 65.0 - 130 °C | 149 - 266 °F | Average value: 115 °C Grade Count:7 |
| UL RTI, Mechanical with Impact | 65.0 - 105 °C | 149 - 221 °F | Average value: 84.0 °C Grade Count:7 |
| UL RTI, Mechanical without Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 97.1 °C Grade Count:7 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:96 |
| Oxygen Index | 22.0 - 39.0 % | 22.0 - 39.0 % | Average value: 31.9 % Grade Count:17 |
| Glow Wire Test | 775 - 960 °C | 1430 - 1760 °F | Average value: 915 °C Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 285 °C Grade Count:9 |
| Feed Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Average value: 75.0 °C Grade Count:4 |
| Nozzle Temperature | 250 - 293 °C | 482 - 560 °F | Average value: 270 °C Grade Count:11 |
| Melt Temperature | 220 - 305 °C | 428 - 581 °F | Average value: 271 °C Grade Count:44 |
| Mold Temperature | 26.7 - 107 °C | 80.0 - 225 °F | Average value: 75.3 °C Grade Count:37 |
| Drying Temperature | 71.1 - 130 °C | 160 - 266 °F | Average value: 84.0 °C Grade Count:30 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.42 hour Grade Count:19 |
| 2.00 - 4.00 hour @Temperature 71.1 - 71.1 °C | 2.00 - 4.00 hour @Temperature 160 - 160 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0300 - 2.20 % | 0.0300 - 2.20 % | Average value: 0.394 % Grade Count:16 |
| Dew Point | -28.9 - -17.8 °C | -20.0 - 0.000 °F | Average value: -20.6 °C Grade Count:4 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 73.1 MPa Grade Count:14 |
| Back Pressure | 0.0689 - 1.72 MPa | 10.0 - 250 psi | Average value: 0.526 MPa Grade Count:4 |
| Screw Speed | 20.0 - 200 rpm | 20.0 - 200 rpm | Average value: 76.0 rpm Grade Count:5 |