- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 112.0
- 断裂伸长率 [%]: 107
- 弯曲强度 [MPa]: 75.8
- 弯曲模量 [MPa]: 2.76
- 硬度: 110.0
- 热变形温度 [℃]: 144.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 - 1.54 g/cc | 0.0426 - 0.0556 lb/in³ | Average value: 1.32 g/cc Grade Count:84 |
| Filler Content | 5.00 - 50.0 % | 5.00 - 50.0 % | Average value: 22.9 % Grade Count:33 |
| Water Absorption | 0.100 - 1.00 % | 0.100 - 1.00 % | Average value: 0.690 % Grade Count:57 |
| Linear Mold Shrinkage | 0.000200 - 0.0160 cm/cm | 0.000200 - 0.0160 in/in | Average value: 0.00270 cm/cm Grade Count:80 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00306 cm/cm Grade Count:18 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00637 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 120 | 110 - 120 | Average value: 118 Grade Count:27 |
| Tensile Strength, Ultimate | 75.8 - 241 MPa | 11000 - 35000 psi | Average value: 175 MPa Grade Count:73 |
| Tensile Strength, Yield | 112 - 200 MPa | 16200 - 29000 psi | Average value: 171 MPa Grade Count:12 |
| Elongation at Break | 0.900 - 182 % | 0.900 - 182 % | Average value: 5.31 % Grade Count:63 |
| Elongation at Yield | 1.10 - 6.00 % | 1.10 - 6.00 % | Average value: 2.86 % Grade Count:22 |
| Modulus of Elasticity | 3.45 - 32.4 GPa | 500 - 4710 ksi | Average value: 16.0 GPa Grade Count:62 |
| Flexural Yield Strength | 107 - 372 MPa | 15500 - 54000 psi | Average value: 260 MPa Grade Count:82 |
| Flexural Modulus | 2.76 - 24.8 GPa | 400 - 3600 ksi | Average value: 12.8 GPa Grade Count:83 |
| Compressive Yield Strength | 89.6 - 172 MPa | 13000 - 25000 psi | Average value: 134 MPa Grade Count:12 |
| Izod Impact, Notched | 0.320 - 2.40 J/cm | 0.600 - 4.50 ft-lb/in | Average value: 0.881 J/cm Grade Count:64 |
| Izod Impact, Unnotched | 3.20 - 10.7 J/cm | 6.00 - 20.0 ft-lb/in | Average value: 6.82 J/cm Grade Count:45 |
| Izod Impact, Notched (ISO) | 5.00 - 10.9 kJ/m² | 2.38 - 5.19 ft-lb/in² | Average value: 8.52 kJ/m² Grade Count:4 |
| Izod Impact, Unnotched (ISO) | 41.0 - 68.5 kJ/m² | 19.5 - 32.6 ft-lb/in² | Average value: 55.2 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 2.60 - 6.50 J/cm² | 12.4 - 30.9 ft-lb/in² | Average value: 4.15 J/cm² Grade Count:18 |
| 3.00 - 4.00 J/cm² @Temperature -30.0 - -30.0 °C | 14.3 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.43 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 0.700 - 1.20 J/cm² | 3.33 - 5.71 ft-lb/in² | Average value: 0.957 J/cm² Grade Count:7 |
| 0.600 - 0.900 J/cm² @Temperature -30.0 - -30.0 °C | 2.86 - 4.28 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.729 J/cm² Grade Count:7 | |
| Coefficient of Friction | 0.0900 - 0.600 | 0.0900 - 0.600 | Average value: 0.196 Grade Count:17 |
| Coefficient of Friction, Static | 0.0700 - 0.560 | 0.0700 - 0.560 | Average value: 0.157 Grade Count:17 |
| K (wear) Factor | 10.1 - 30.2 x 10-8 mm³/N-M | 5.00 - 15.0 x 10-10 in³-min/ft-lb-hr | Average value: 16.8 x 10-8 mm³/N-M Grade Count:8 |
| Limiting Pressure Velocity | 0.771 - 3.30 MPa-m/sec | 22000 - 94200 psi-ft/min | Average value: 1.45 MPa-m/sec Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.100 - 1.00e+8 ohm-cm | 0.100 - 1.00e+8 ohm-cm | Average value: 1.10e+6 ohm-cm Grade Count:46 |
| Surface Resistance | 1.00 - 1.00e+10 ohm | 1.00 - 1.00e+10 ohm | Average value: 3.57e+8 ohm Grade Count:28 |
| Insulation Resistance | 1000 - 1.00e+10 ohm | 1000 - 1.00e+10 ohm | Average value: 5.56e+8 ohm Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 80.0 µm/m-°C | 7.78 - 44.4 µin/in-°F | Average value: 25.5 µm/m-°C Grade Count:29 |
| Thermal Conductivity | 0.330 - 1.15 W/m-K | 2.29 - 8.00 BTU-in/hr-ft²-°F | Average value: 0.553 W/m-K Grade Count:15 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 261 °C Grade Count:6 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 137 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 - 262 °C | 292 - 504 °F | Average value: 249 °C Grade Count:32 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 - 260 °C | 283 - 500 °F | Average value: 245 °C Grade Count:71 |
| Vicat Softening Point | 200 - 255 °C | 392 - 491 °F | Average value: 239 °C Grade Count:11 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:37 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 - 293 °C | 525 - 560 °F | Average value: 287 °C Grade Count:42 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:19 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 296 °C Grade Count:43 |
| Mold Temperature | 65.6 - 121 °C | 150 - 250 °F | Average value: 93.7 °C Grade Count:62 |
| Drying Temperature | 75.0 - 107 °C | 167 - 225 °F | Average value: 87.3 °C Grade Count:41 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:17 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:18 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:15 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 101 MPa Grade Count:34 |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | Average value: 0.259 MPa Grade Count:3 |