- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 83.0
- 断裂伸长率 [%]: 100
- 弯曲强度 [MPa]: 82.7
- 弯曲模量 [MPa]: 2.60
- 硬度: 115.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.37 g/cc | 0.0412 - 0.0495 lb/in³ | Average value: 1.19 g/cc Grade Count:10 |
| Water Absorption | 0.300 - 1.80 % | 0.300 - 1.80 % | Average value: 0.957 % Grade Count:7 |
| Water Absorption at Saturation | 2.50 - 8.50 % | 2.50 - 8.50 % | Average value: 7.11 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00500 - 0.0170 cm/cm | 0.00500 - 0.0170 in/in | Average value: 0.0107 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 79.0 - 101 | 79.0 - 101 | Average value: 88.3 Grade Count:4 |
| Hardness, Rockwell R | 115 - 120 | 115 - 120 | Average value: 117 Grade Count:5 |
| Hardness, Shore D | 80.0 - 82.0 | 80.0 - 82.0 | Average value: 80.7 Grade Count:3 |
| Tensile Strength, Ultimate | 82.7 - 138 MPa | 12000 - 20000 psi | Average value: 97.8 MPa Grade Count:5 |
| Tensile Strength, Yield | 83.0 - 179 MPa | 12000 - 26000 psi | Average value: 104 MPa Grade Count:5 |
| Elongation at Break | 3.00 - 90.0 % | 3.00 - 90.0 % | Average value: 47.2 % Grade Count:10 |
| Modulus of Elasticity | 2.93 - 3.70 GPa | 425 - 537 ksi | Average value: 3.30 GPa Grade Count:4 |
| Flexural Yield Strength | 100 - 269 MPa | 14500 - 39000 psi | Average value: 148 MPa Grade Count:8 |
| Flexural Modulus | 2.60 - 9.65 GPa | 377 - 1400 ksi | Average value: 4.14 GPa Grade Count:10 |
| Compressive Yield Strength | 32.0 - 100 MPa | 4640 - 14500 psi | Average value: 74.0 MPa Grade Count:3 |
| Izod Impact, Notched | 0.320 - 1.12 J/cm | 0.600 - 2.10 ft-lb/in | Average value: 0.762 J/cm Grade Count:7 |
| Coefficient of Friction | 0.250 - 0.600 | 0.250 - 0.600 | Average value: 0.333 Grade Count:3 |
| Limiting Pressure Velocity | 0.0800 - 0.130 MPa-m/sec | 2280 - 3710 psi-ft/min | Average value: 0.101 MPa-m/sec Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 1.00e+15 ohm-cm | 1.00e+11 - 1.00e+15 ohm-cm | Average value: 7.29e+14 ohm-cm Grade Count:7 |
| Surface Resistance | 1.00e+12 - 1.00e+13 ohm | 1.00e+12 - 1.00e+13 ohm | Average value: 7.00e+12 ohm Grade Count:3 |
| Dielectric Constant | 3.50 - 4.30 | 3.50 - 4.30 | Average value: 3.76 Grade Count:6 |
| Dielectric Strength | 11.8 - 30.5 kV/mm | 300 - 775 kV/in | Average value: 22.5 kV/mm Grade Count:7 |
| Dissipation Factor | 0.0130 - 0.0240 | 0.0130 - 0.0240 | Average value: 0.0190 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 100 µm/m-°C | 11.0 - 55.6 µin/in-°F | Average value: 69.4 µm/m-°C Grade Count:6 |
| 90.0 - 90.0 µm/m-°C @Temperature 93.3 - 238 °C | 50.0 - 50.0 µin/in-°F @Temperature 200 - 460 °F | Average value: 90.0 µm/m-°C Grade Count:1 | |
| Thermal Conductivity | 0.230 - 0.280 W/m-K | 1.60 - 1.94 BTU-in/hr-ft²-°F | Average value: 0.252 W/m-K Grade Count:3 |
| Melting Point | 254 - 265 °C | 489 - 509 °F | Average value: 258 °C Grade Count:7 |
| Maximum Service Temperature, Air | 80.0 - 241 °C | 176 - 466 °F | Average value: 130 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 - 259 °C | 392 - 499 °F | Average value: 230 °C Grade Count:8 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 256 °C | 158 - 492 °F | Average value: 125 °C Grade Count:10 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:4 |