- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.2
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 68.9
- 断裂伸长率 [%]: 115
- 弯曲强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.03
- 硬度: 105.0
- 热变形温度 [℃]: 224.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | Average value: 1.14 g/cc Grade Count:11 |
| Water Absorption | 1.20 - 1.50 % | 1.20 - 1.50 % | Average value: 1.33 % Grade Count:7 |
| Linear Mold Shrinkage | 0.0100 - 0.0180 cm/cm | 0.0100 - 0.0180 in/in | Average value: 0.0140 cm/cm Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 - 109 | 105 - 109 | Average value: 106 Grade Count:3 |
| Tensile Strength, Ultimate | 85.0 - 90.0 MPa | 12300 - 13100 psi | Average value: 88.2 MPa Grade Count:3 |
| Tensile Strength, Yield | 68.9 - 90.0 MPa | 10000 - 13100 psi | Average value: 83.2 MPa Grade Count:8 |
| Elongation at Break | 7.00 - 60.0 % | 7.00 - 60.0 % | Average value: 33.0 % Grade Count:10 |
| Flexural Yield Strength | 115 - 138 MPa | 16700 - 20000 psi | Average value: 127 MPa Grade Count:10 |
| 29.9922 - 29.9922 MPa @Temperature 90.0 - 90.0 °C | 4350.01 - 4350.01 psi @Temperature 194 - 194 °F | Average value: 30.0 MPa Grade Count:1 | |
| Flexural Modulus | 2.03 - 3.25 GPa | 295 - 471 ksi | Average value: 2.93 GPa Grade Count:11 |
| Izod Impact, Notched | 0.400 - 0.587 J/cm | 0.749 - 1.10 ft-lb/in | Average value: 0.503 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 3.99 - 3.99 kJ/m² @Temperature -30.0 - -30.0 °C | 1.90 - 1.90 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.99 kJ/m² Grade Count:1 |
| Charpy Impact, Notched | 0.380 - 0.380 J/cm² @Temperature -30.0 - -30.0 °C | 1.81 - 1.81 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.380 J/cm² Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+18 ohm-cm | 1.00e+12 - 1.00e+18 ohm-cm | Average value: 2.50e+17 ohm-cm Grade Count:4 |
| Dielectric Strength | 16.9 - 21.7 kV/mm | 430 - 550 kV/in | Average value: 18.3 kV/mm Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.2 - 77.4 µm/m-°C | 39.0 - 43.0 µin/in-°F | Average value: 75.6 µm/m-°C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 - 237 °C | 435 - 459 °F | Average value: 233 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 - 90.6 °C | 162 - 195 °F | Average value: 81.8 °C Grade Count:11 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 263 - 293 °C | 505 - 560 °F | Average value: 275 °C Grade Count:3 |
| Melt Temperature | 241 - 304 °C | 465 - 580 °F | Average value: 272 °C Grade Count:5 |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | Average value: 73.9 °C Grade Count:3 |
| Drying Temperature | 71.1 - 79.4 °C | 160 - 175 °F | Average value: 76.7 °C Grade Count:3 |
| Dry Time | 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:1 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 43.2 MPa Grade Count:3 |
| Back Pressure | 0.0689 - 1.72 MPa | 10.0 - 250 psi | Average value: 0.586 MPa Grade Count:3 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 60.0 rpm Grade Count:3 |