- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 75.2
- 断裂伸长率 [%]: 110
- 弯曲强度 [MPa]: 200.0
- 弯曲模量 [MPa]: 10.7
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 - 1.50 g/cc | 0.0459 - 0.0542 lb/in³ | Average value: 1.36 g/cc Grade Count:16 |
| Filler Content | 35.0 - 40.0 % | 35.0 - 40.0 % | Average value: 39.2 % Grade Count:6 |
| Water Absorption | 0.400 - 5.00 % | 0.400 - 5.00 % | Average value: 1.66 % Grade Count:10 |
| Viscosity Measurement | 0.560 - 145 | 0.560 - 145 | Average value: 96.9 Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 - 0.0150 cm/cm | 0.000500 - 0.0150 in/in | Average value: 0.00328 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 cm/cm | 0.00200 in/in | Average value: 0.00200 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 200 - 331 MPa | 29000 - 48000 psi | Average value: 264 MPa Grade Count:12 |
| Tensile Strength, Yield | 75.2 - 195 MPa | 10900 - 28300 psi | Average value: 120 MPa Grade Count:3 |
| Elongation at Break | 1.00 - 75.0 % | 1.00 - 75.0 % | Average value: 7.40 % Grade Count:14 |
| Modulus of Elasticity | 4.50 - 42.7 GPa | 653 - 6200 ksi | Average value: 23.7 GPa Grade Count:13 |
| Flexural Yield Strength | 110 - 483 MPa | 16000 - 70100 psi | Average value: 351 MPa Grade Count:14 |
| Flexural Modulus | 10.7 - 33.1 GPa | 1550 - 4800 ksi | Average value: 22.0 GPa Grade Count:12 |
| Izod Impact, Notched | 0.530 - 3.10 J/cm | 0.993 - 5.81 ft-lb/in | Average value: 1.48 J/cm Grade Count:13 |
| Izod Impact, Unnotched | 10.7 - 11.7 J/cm | 20.0 - 22.0 ft-lb/in | Average value: 10.9 J/cm Grade Count:6 |
| Charpy Impact Unnotched | 1.80 - 9.50 J/cm² | 8.57 - 45.2 ft-lb/in² | Average value: 4.05 J/cm² Grade Count:4 |
| 3.00 - 8.00 J/cm² @Temperature -40.0 - -20.0 °C | 14.3 - 38.1 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 4.67 J/cm² Grade Count:3 | |
| Charpy Impact, Notched | 0.500 - 1.30 J/cm² | 2.38 - 6.19 ft-lb/in² | Average value: 0.813 J/cm² Grade Count:3 |
| 0.700 - 1.20 J/cm² @Temperature -30.0 - -20.0 °C | 3.33 - 5.71 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.950 J/cm² Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+15 ohm-cm | 1.00 - 1.00e+15 ohm-cm | Average value: 1.00e+14 ohm-cm Grade Count:10 |
| Surface Resistance | 10.0 - 1.00e+14 ohm | 10.0 - 1.00e+14 ohm | Average value: 2.02e+13 ohm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 - 16.2 µm/m-°C | 8.00 - 9.00 µin/in-°F | Average value: 14.8 µm/m-°C Grade Count:4 |
| Melting Point | 221 - 260 °C | 430 - 500 °F | Average value: 248 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 - 265 °C | 464 - 509 °F | Average value: 256 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 - 260 °C | 248 - 500 °F | Average value: 232 °C Grade Count:15 |
| Vicat Softening Point | 200 - 256 °C | 392 - 493 °F | Average value: 227 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 - 293 °C | 525 - 560 °F | Average value: 284 °C Grade Count:3 |
| Nozzle Temperature | 271 - 304 °C | 520 - 580 °F | Average value: 288 °C Grade Count:3 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 286 °C Grade Count:8 |
| Mold Temperature | 65.6 - 107 °C | 150 - 225 °F | Average value: 86.8 °C Grade Count:11 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 84.1 °C Grade Count:6 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.67 hour Grade Count:3 |
| Moisture Content | 0.150 - 0.200 % | 0.150 - 0.200 % | Average value: 0.178 % Grade Count:4 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 96.8 MPa Grade Count:6 |