- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.374
- 拉伸强度 [MPa]: 46.9
- 断裂伸长率 [%]: 75.8
- 弯曲强度 [MPa]: 58.6
- 弯曲模量 [MPa]: 2.07
- 硬度: 98.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.60 g/cc | 0.0405 - 0.0578 lb/in³ | Average value: 1.29 g/cc Grade Count:116 |
| Filler Content | 5.00 - 50.0 % | 5.00 - 50.0 % | Average value: 23.3 % Grade Count:34 |
| Water Absorption | 0.300 - 6.40 % | 0.300 - 6.40 % | Average value: 0.943 % Grade Count:70 |
| Moisture Absorption at Equilibrium | 0.450 - 2.70 % | 0.450 - 2.70 % | Average value: 1.71 % Grade Count:19 |
| Water Absorption at Saturation | 4.50 - 6.40 % | 4.50 - 6.40 % | Average value: 5.50 % Grade Count:4 |
| Linear Mold Shrinkage | 0.000600 - 0.0160 cm/cm | 0.000600 - 0.0160 in/in | Average value: 0.00516 cm/cm Grade Count:105 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.0150 cm/cm | 0.00200 - 0.0150 in/in | Average value: 0.00685 cm/cm Grade Count:23 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0130 cm/cm | 0.00700 - 0.0130 in/in | Average value: 0.00929 cm/cm Grade Count:14 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76.0 - 95.0 | 76.0 - 95.0 | Average value: 87.1 Grade Count:14 |
| Hardness, Rockwell R | 98.0 - 122 | 98.0 - 122 | Average value: 115 Grade Count:63 |
| Tensile Strength, Ultimate | 58.6 - 221 MPa | 8500 - 32100 psi | Average value: 116 MPa Grade Count:77 |
| Tensile Strength, Yield | 46.9 - 159 MPa | 6800 - 23000 psi | Average value: 117 MPa Grade Count:39 |
| Elongation at Break | 2.00 - 12.0 % | 2.00 - 12.0 % | Average value: 4.28 % Grade Count:111 |
| Elongation at Yield | 3.00 - 6.00 % | 3.00 - 6.00 % | Average value: 3.85 % Grade Count:4 |
| Modulus of Elasticity | 2.76 - 15.2 GPa | 400 - 2200 ksi | Average value: 7.04 GPa Grade Count:54 |
| Flexural Yield Strength | 75.8 - 360 MPa | 11000 - 52200 psi | Average value: 168 MPa Grade Count:93 |
| Flexural Modulus | 2.07 - 36.2 GPa | 300 - 5250 ksi | Average value: 6.19 GPa Grade Count:102 |
| Compressive Yield Strength | 28.0 - 179 MPa | 4060 - 26000 psi | Average value: 120 MPa Grade Count:22 |
| Izod Impact, Notched | 0.374 - 6.51 J/cm | 0.700 - 12.2 ft-lb/in | Average value: 1.65 J/cm Grade Count:91 |
| 1.0678 - 1.0678 J/cm @Temperature -40.0 - -40.0 °C | 2.0004 - 2.0004 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.07 J/cm Grade Count:9 | |
| 1.0678 - 1.0678 J/cm @Thickness 3.17 - 3.17 mm | 2.0004 - 2.0004 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.07 J/cm Grade Count:9 | |
| Izod Impact, Unnotched | 4.64 - 5340 J/cm | 8.69 - 10000 ft-lb/in | Average value: 8.58 J/cm Grade Count:46 |
| Izod Impact, Notched (ISO) | 2.94 - 22.5 kJ/m² | 1.40 - 10.7 ft-lb/in² | Average value: 14.2 kJ/m² Grade Count:12 |
| 9.00 - 19.0 kJ/m² @Temperature -30.0 - -30.0 °C | 4.28 - 9.04 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 13.0 kJ/m² Grade Count:6 | |
| Izod Impact, Unnotched (ISO) | 85.0 - 90.0 kJ/m² | 40.4 - 42.8 ft-lb/in² | Average value: 87.5 kJ/m² Grade Count:4 |
| 75.0 - 95.0 kJ/m² @Temperature -30.0 - -30.0 °C | 35.7 - 45.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 80.0 kJ/m² Grade Count:4 | |
| Charpy Impact Unnotched | 3.50 - 10.5 J/cm² | 16.7 - 50.0 ft-lb/in² | Average value: 7.58 J/cm² Grade Count:15 |
| 3.50 - 8.70 J/cm² @Temperature -30.0 - -30.0 °C | 16.7 - 41.4 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.30 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 0.600 - 4.00 J/cm² | 2.86 - 19.0 ft-lb/in² | Average value: 2.21 J/cm² Grade Count:18 |
| 0.500 - 1.80 J/cm² @Temperature -30.0 - -30.0 °C | 2.38 - 8.57 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.19 J/cm² Grade Count:9 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+15 ohm-cm | 10.0 - 1.00e+15 ohm-cm | Average value: 2.03e+14 ohm-cm Grade Count:66 |
| Surface Resistance | 1.00e+6 - 1.00e+15 ohm | 1.00e+6 - 1.00e+15 ohm | Average value: 4.05e+13 ohm Grade Count:30 |
| Dielectric Constant | 3.50 - 6.90 | 3.50 - 6.90 | Average value: 4.22 Grade Count:19 |
| Dielectric Strength | 11.8 - 90.0 kV/mm | 300 - 2290 kV/in | Average value: 24.2 kV/mm Grade Count:45 |
| Dissipation Factor | 0.0130 - 0.0200 | 0.0130 - 0.0200 | Average value: 0.0152 Grade Count:10 |
| Dielectric Loss Index | 0.0120 - 0.190 | 0.0120 - 0.190 | Average value: 0.0751 Grade Count:7 |
| Arc Resistance | 82.0 - 90.0 sec | 82.0 - 90.0 sec | Average value: 85.8 sec Grade Count:8 |
| Comparative Tracking Index | 350 - 550 V | 350 - 550 V | Average value: 500 V Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 13.0 - 82.8 µm/m-°C | 7.22 - 46.0 µin/in-°F | Average value: 54.3 µm/m-°C Grade Count:42 |
| Thermal Conductivity | 0.300 - 0.504 W/m-K | 2.08 - 3.50 BTU-in/hr-ft²-°F | Average value: 0.426 W/m-K Grade Count:10 |
| Melting Point | 252 - 275 °C | 486 - 527 °F | Average value: 258 °C Grade Count:48 |
| Maximum Service Temperature, Air | 110 - 250 °C | 230 - 482 °F | Average value: 160 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 304 °C | 410 - 580 °F | Average value: 248 °C Grade Count:88 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 - 252 °C | 167 - 486 °F | Average value: 228 °C Grade Count:104 |
| Vicat Softening Point | 228 - 245 °C | 442 - 473 °F | Average value: 234 °C Grade Count:9 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:77 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 285 °C Grade Count:38 |
| Feed Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Average value: 72.5 °C Grade Count:4 |
| Nozzle Temperature | 250 - 304 °C | 482 - 580 °F | Average value: 283 °C Grade Count:4 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 284 °C Grade Count:17 |
| Mold Temperature | 50.0 - 110 °C | 122 - 230 °F | Average value: 85.7 °C Grade Count:49 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 82.1 °C Grade Count:11 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.36 hour Grade Count:7 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:3 | |
| Moisture Content | 0.180 - 1.60 % | 0.180 - 1.60 % | Average value: 0.336 % Grade Count:10 |
| Injection Pressure | 4.96 - 124 MPa | 720 - 18000 psi | Average value: 93.5 MPa Grade Count:34 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:3 |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | Average value: 0.862 MPa Grade Count:3 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:3 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 65.0 rpm Grade Count:3 |