- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.63
- 拉伸强度 [MPa]: 123.0
- 弯曲模量 [MPa]: 5.90
- 热变形温度 [℃]: 255.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | Dry; ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | Wet |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55 | 55 | Wet; ASTM D785 |
| 95 | 95 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 123 MPa | 17800 psi | Wet; ASTM D638 |
| 153 MPa | 22200 psi | Dry; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Dry; ASTM D638 |
| 2.7 % | 2.7 % | Wet; ASTM D638 | |
| Flexural Strength | 177 MPa | 25700 psi | Wet; ASTM D790 |
| 216 MPa | 31300 psi | Dry; ASTM D790 | |
| Flexural Modulus | 5.90 GPa | 856 ksi | Wet; ASTM D790 |
| 7.60 GPa | 1100 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | Dry; ASTM D256 |
| 0.720 J/cm | 1.35 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 24 | 24 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Dry; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | Dry |
| Oxygen Index | 37 % | 37 % | Dry; ASTM D2863 |