- 吸水率 [%]: 1.5
- 缺口冲击强度: 0.34
- 拉伸强度 [MPa]: 64.0
- 弯曲模量 [MPa]: 2.90
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | Wet |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | Dry; ASTM D785 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Wet; ASTM D638 |
| 88.0 MPa | 12800 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 3.5 % | 3.5 % | Wet; ASTM D638 | |
| Flexural Strength | 93.0 MPa | 13500 psi | Wet; ASTM D790 |
| 147 MPa | 21300 psi | Dry; ASTM D790 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | Wet; ASTM D790 |
| 5.90 GPa | 856 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | Dry; ASTM D256 |
| 0.390 J/cm | 0.731 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | Dry; ASTM D648 |