- 吸水率 [%]: 1.2
- 缺口冲击强度: 6.68
- 拉伸强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 1.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.016 cm/cm @Thickness 3.17 mm | 0.016 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 74.0 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 1.862 GPa | 270.1 ksi | ASTM D790 |
| Izod Impact, Notched | 6.68 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 12.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |