- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 2.1
- 缺口冲击强度: 7.0
- 硬度: 115.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.8 % @Temperature 23.0 °C | 6.8 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85 | 85 | 50%RH; ISO 2039/2 | ||
| 102 | 102 | DAM; ISO 2039/2 | |||
| Hardness, Rockwell R | 115 | 115 | 50%RH; ISO 2039/2 | ||
| 122 | 122 | DAM; ISO 2039/2 | |||
| Tensile Strength at Break | 103 MPa @Temperature 23.0 °C | 14900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 159 MPa @Temperature 23.0 °C | 23100 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Stress | 17.5 MPa @Strain 0.530 %, Temperature 120 °C | 2540 psi @Strain 0.530 %, Temperature 248 °F | 50%RH; ISO 527 | ||
| 18.5 MPa @Strain 0.520 %, Temperature 90.0 °C | 2680 psi @Strain 0.520 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 20.5 MPa @Strain 0.520 %, Temperature 60.0 °C | 2970 psi @Strain 0.520 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 22.2 MPa @Strain 0.630 %, Temperature 120 °C | 3220 psi @Strain 0.630 %, Temperature 248 °F | DAM; ISO 527 | |||
| 23.0 MPa @Strain 0.480 %, Temperature 40.0 °C | 3340 psi @Strain 0.480 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 24.5 MPa @Strain 0.610 %, Temperature 90.0 °C | 3550 psi @Strain 0.610 %, Temperature 194 °F | DAM; ISO 527 | |||
| 25.9 MPa @Strain 0.440 %, Temperature 23.0 °C | 3760 psi @Strain 0.440 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 26.2 MPa @Strain 0.460 %, Temperature 60.0 °C | 3800 psi @Strain 0.460 %, Temperature 140 °F | DAM; ISO 527 | |||
| 27.7 MPa @Strain 0.270 %, Temperature -20.0 °C | 4020 psi @Strain 0.270 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 28.8 MPa @Strain 0.330 %, Temperature 0.000 °C | 4180 psi @Strain 0.330 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 30.6 MPa @Strain 1.06 %, Temperature 120 °C | 4440 psi @Strain 1.06 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 33.2 MPa @Strain 0.360 %, Temperature 40.0 °C | 4820 psi @Strain 0.360 %, Temperature 104 °F | DAM; ISO 527 | |||
| 33.4 MPa @Strain 1.04 %, Temperature 90.0 °C | 4840 psi @Strain 1.04 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 35.9 MPa @Strain 0.250 %, Temperature 23.0 °C | 5210 psi @Strain 0.250 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 37.4 MPa @Strain 1.04 %, Temperature 60.0 °C | 5420 psi @Strain 1.04 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 38.3 MPa @Strain 1.26 %, Temperature 120 °C | 5550 psi @Strain 1.26 %, Temperature 248 °F | DAM; ISO 527 | |||
| 40.4 MPa @Strain 1.59 %, Temperature 120 °C | 5860 psi @Strain 1.59 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 41.2 MPa @Strain 0.960 %, Temperature 40.0 °C | 5980 psi @Strain 0.960 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 42.0 MPa @Strain 1.22 %, Temperature 90.0 °C | 6090 psi @Strain 1.22 %, Temperature 194 °F | DAM; ISO 527 | |||
| 45.1 MPa @Strain 1.56 %, Temperature 90.0 °C | 6540 psi @Strain 1.56 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 45.4 MPa @Strain 0.920 %, Temperature 60.0 °C | 6580 psi @Strain 0.920 %, Temperature 140 °F | DAM; ISO 527 | |||
| 46.8 MPa @Strain 0.880 %, Temperature 23.0 °C | 6790 psi @Strain 0.880 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 47.6 MPa @Strain 2.12 %, Temperature 120 °C | 6900 psi @Strain 2.12 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 50.2 MPa @Strain 1.89 %, Temperature 120 °C | 7280 psi @Strain 1.89 %, Temperature 248 °F | DAM; ISO 527 | |||
| 50.7 MPa @Strain 1.56 %, Temperature 60.0 °C | 7350 psi @Strain 1.56 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 51.2 MPa @Strain 0.540 %, Temperature -20.0 °C | 7430 psi @Strain 0.540 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 52.4 MPa @Strain 0.660 %, Temperature 0.000 °C | 7600 psi @Strain 0.660 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 52.8 MPa @Strain 2.65 %, Temperature 120 °C | 7660 psi @Strain 2.65 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 53.9 MPa @Strain 2.08 %, Temperature 90.0 °C | 7820 psi @Strain 2.08 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 55.4 MPa @Strain 1.44 %, Temperature 40.0 °C | 8040 psi @Strain 1.44 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 55.7 MPa @Strain 1.83 %, Temperature 90.0 °C | 8080 psi @Strain 1.83 %, Temperature 194 °F | DAM; ISO 527 | |||
| 56.5 MPa @Strain 3.18 %, Temperature 120 °C | 8190 psi @Strain 3.18 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 57.7 MPa @Strain 0.720 %, Temperature 40.0 °C | 8370 psi @Strain 0.720 %, Temperature 104 °F | DAM; ISO 527 | |||
| 58.8 MPa @Strain 2.52 %, Temperature 120 °C | 8530 psi @Strain 2.52 %, Temperature 248 °F | DAM; ISO 527 | |||
| 59.0 MPa @Strain 3.71 %, Temperature 120 °C | 8560 psi @Strain 3.71 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 60.0 MPa @Strain 0.500 %, Temperature 23.0 °C | 8700 psi @Strain 0.500 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 60.4 MPa @Strain 2.60 %, Temperature 90.0 °C | 8760 psi @Strain 2.60 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 60.7 MPa @Strain 4.24 %, Temperature 120 °C | 8800 psi @Strain 4.24 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 61.0 MPa @Strain 1.38 %, Temperature 60.0 °C | 8850 psi @Strain 1.38 %, Temperature 140 °F | DAM; ISO 527 | |||
| 61.1 MPa @Strain 2.08 %, Temperature 60.0 °C | 8860 psi @Strain 2.08 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 61.7 MPa @Strain 4.77 %, Temperature 120 °C | 8950 psi @Strain 4.77 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 62.2 MPa @Strain 5.30 %, Temperature 120 °C | 9020 psi @Strain 5.30 %, Temperature 248 °F | 50%RH; Break; ISO 527 | |||
| 63.2 MPa @Strain 1.32 %, Temperature 23.0 °C | 9170 psi @Strain 1.32 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 64.5 MPa @Strain 3.15 %, Temperature 120 °C | 9350 psi @Strain 3.15 %, Temperature 248 °F | DAM; ISO 527 | |||
| 65.1 MPa @Strain 3.12 %, Temperature 90.0 °C | 9440 psi @Strain 3.12 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 66.0 MPa @Strain 2.44 %, Temperature 90.0 °C | 9570 psi @Strain 2.44 %, Temperature 194 °F | DAM; ISO 527 | |||
| 66.4 MPa @Strain 1.92 %, Temperature 40.0 °C | 9630 psi @Strain 1.92 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 68.1 MPa @Strain 3.78 %, Temperature 120 °C | 9880 psi @Strain 3.78 %, Temperature 248 °F | DAM; ISO 527 | |||
| 68.2 MPa @Strain 3.64 %, Temperature 90.0 °C | 9890 psi @Strain 3.64 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 68.8 MPa @Strain 2.60 %, Temperature 60.0 °C | 9980 psi @Strain 2.60 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 70.1 MPa @Strain 4.41 %, Temperature 120 °C | 10200 psi @Strain 4.41 %, Temperature 248 °F | DAM; ISO 527 | |||
| 70.3 MPa @Strain 4.16 %, Temperature 90.0 °C | 10200 psi @Strain 4.16 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 71.3 MPa @Strain 5.04 %, Temperature 120 °C | 10300 psi @Strain 5.04 %, Temperature 248 °F | DAM; ISO 527 | |||
| 71.4 MPa @Strain 4.68 %, Temperature 90.0 °C | 10400 psi @Strain 4.68 %, Temperature 194 °F | 50%RH; ISO 527 | |||
| 71.4 MPa @Strain 0.810 %, Temperature -20.0 °C | 10400 psi @Strain 0.810 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 71.9 MPa @Strain 5.20 %, Temperature 90.0 °C | 10400 psi @Strain 5.20 %, Temperature 194 °F | 50%RH; Break; ISO 527 | |||
| 72.0 MPa @Strain 0.990 %, Temperature 0.000 °C | 10400 psi @Strain 0.990 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 72.3 MPa @Strain 5.67 %, Temperature 120 °C | 10500 psi @Strain 5.67 %, Temperature 248 °F | DAM; ISO 527 | |||
| 72.7 MPa @Strain 6.30 %, Temperature 120 °C | 10500 psi @Strain 6.30 %, Temperature 248 °F | DAM; Break; ISO 527 | |||
| 73.4 MPa @Strain 1.84 %, Temperature 60.0 °C | 10600 psi @Strain 1.84 %, Temperature 140 °F | DAM; ISO 527 | |||
| 73.5 MPa @Strain 3.05 %, Temperature 90.0 °C | 10700 psi @Strain 3.05 %, Temperature 194 °F | DAM; ISO 527 | |||
| 74.4 MPa @Strain 3.12 %, Temperature 60.0 °C | 10800 psi @Strain 3.12 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 74.8 MPa @Strain 2.40 %, Temperature 40.0 °C | 10800 psi @Strain 2.40 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 76.0 MPa @Strain 1.76 %, Temperature 23.0 °C | 11000 psi @Strain 1.76 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 77.8 MPa @Strain 1.08 %, Temperature 40.0 °C | 11300 psi @Strain 1.08 %, Temperature 104 °F | DAM; ISO 527 | |||
| 78.3 MPa @Strain 3.64 %, Temperature 60.0 °C | 11400 psi @Strain 3.64 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 78.7 MPa @Strain 3.66 %, Temperature 90.0 °C | 11400 psi @Strain 3.66 %, Temperature 194 °F | DAM; ISO 527 | |||
| 80.1 MPa @Strain 0.750 %, Temperature 23.0 °C | 11600 psi @Strain 0.750 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 80.9 MPa @Strain 4.16 %, Temperature 60.0 °C | 11700 psi @Strain 4.16 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 81.1 MPa @Strain 2.88 %, Temperature 40.0 °C | 11800 psi @Strain 2.88 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 81.9 MPa @Strain 4.27 %, Temperature 90.0 °C | 11900 psi @Strain 4.27 %, Temperature 194 °F | DAM; ISO 527 | |||
| 82.4 MPa @Strain 4.68 %, Temperature 60.0 °C | 12000 psi @Strain 4.68 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 83.0 MPa @Strain 2.30 %, Temperature 60.0 °C | 12000 psi @Strain 2.30 %, Temperature 140 °F | DAM; ISO 527 | |||
| 83.1 MPa @Strain 5.20 %, Temperature 60.0 °C | 12100 psi @Strain 5.20 %, Temperature 140 °F | 50%RH; Break; ISO 527 | |||
| 83.6 MPa @Strain 4.88 %, Temperature 90.0 °C | 12100 psi @Strain 4.88 %, Temperature 194 °F | DAM; ISO 527 | |||
| 84.5 MPa @Strain 5.49 %, Temperature 90.0 °C | 12300 psi @Strain 5.49 %, Temperature 194 °F | DAM; ISO 527 | |||
| 84.8 MPa @Strain 6.10 %, Temperature 90.0 °C | 12300 psi @Strain 6.10 %, Temperature 194 °F | DAM; Break; ISO 527 | |||
| 85.6 MPa @Strain 2.20 %, Temperature 23.0 °C | 12400 psi @Strain 2.20 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 85.7 MPa @Strain 3.36 %, Temperature 40.0 °C | 12400 psi @Strain 3.36 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 88.3 MPa @Strain 1.32 %, Temperature 0.000 °C | 12800 psi @Strain 1.32 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 89.0 MPa @Strain 3.84 %, Temperature 40.0 °C | 12900 psi @Strain 3.84 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 89.0 MPa @Strain 1.08 %, Temperature -20.0 °C | 12900 psi @Strain 1.08 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 90.3 MPa @Strain 2.76 %, Temperature 60.0 °C | 13100 psi @Strain 2.76 %, Temperature 140 °F | DAM; ISO 527 | |||
| 91.2 MPa @Strain 4.32 %, Temperature 40.0 °C | 13200 psi @Strain 4.32 %, Temperature 104 °F | 50%RH; ISO 527 | |||
| 92.6 MPa @Strain 4.80 %, Temperature 40.0 °C | 13400 psi @Strain 4.80 %, Temperature 104 °F | 50%RH; Break; ISO 527 | |||
| 92.8 MPa @Strain 2.64 %, Temperature 23.0 °C | 13500 psi @Strain 2.64 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 94.0 MPa @Strain 1.44 %, Temperature 40.0 °C | 13600 psi @Strain 1.44 %, Temperature 104 °F | DAM; ISO 527 | |||
| 95.6 MPa @Strain 3.22 %, Temperature 60.0 °C | 13900 psi @Strain 3.22 %, Temperature 140 °F | DAM; ISO 527 | |||
| 96.8 MPa @Strain 1.00 %, Temperature 23.0 °C | 14000 psi @Strain 1.00 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 98.0 MPa @Strain 3.08 %, Temperature 23.0 °C | 14200 psi @Strain 3.08 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 99.0 MPa @Strain 3.68 %, Temperature 60.0 °C | 14400 psi @Strain 3.68 %, Temperature 140 °F | DAM; ISO 527 | |||
| 102 MPa @Strain 4.14 %, Temperature 60.0 °C | 14800 psi @Strain 4.14 %, Temperature 140 °F | DAM; ISO 527 | |||
| 102 MPa @Strain 3.52 %, Temperature 23.0 °C | 14800 psi @Strain 3.52 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 102 MPa @Strain 1.65 %, Temperature 0.000 °C | 14800 psi @Strain 1.65 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 104 MPa @Strain 3.96 %, Temperature 23.0 °C | 15100 psi @Strain 3.96 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 104 MPa @Strain 4.60 %, Temperature 60.0 °C | 15100 psi @Strain 4.60 %, Temperature 140 °F | DAM; Break; ISO 527 | |||
| 105 MPa @Strain 1.35 %, Temperature -20.0 °C | 15200 psi @Strain 1.35 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 105 MPa @Strain 4.40 %, Temperature 23.0 °C | 15200 psi @Strain 4.40 %, Temperature 73.4 °F | 50%RH; Break; ISO 527 | |||
| 107 MPa @Strain 1.80 %, Temperature 40.0 °C | 15500 psi @Strain 1.80 %, Temperature 104 °F | DAM; ISO 527 | |||
| 111 MPa @Strain 1.25 %, Temperature 23.0 °C | 16100 psi @Strain 1.25 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 114 MPa @Strain 1.98 %, Temperature 0.000 °C | 16500 psi @Strain 1.98 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 116 MPa @Strain 2.16 %, Temperature 40.0 °C | 16800 psi @Strain 2.16 %, Temperature 104 °F | DAM; ISO 527 | |||
| 118 MPa @Strain 1.62 %, Temperature -20.0 °C | 17100 psi @Strain 1.62 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 122 MPa @Strain 1.50 %, Temperature 23.0 °C | 17700 psi @Strain 1.50 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 124 MPa @Strain 2.31 %, Temperature 0.000 °C | 18000 psi @Strain 2.31 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 124 MPa @Strain 2.52 %, Temperature 40.0 °C | 18000 psi @Strain 2.52 %, Temperature 104 °F | DAM; ISO 527 | |||
| 129 MPa @Strain 2.88 %, Temperature 40.0 °C | 18700 psi @Strain 2.88 %, Temperature 104 °F | DAM; ISO 527 | |||
| 131 MPa @Strain 1.89 %, Temperature -20.0 °C | 19000 psi @Strain 1.89 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 132 MPa @Strain 2.64 %, Temperature 0.000 °C | 19100 psi @Strain 2.64 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 132 MPa @Strain 1.75 %, Temperature 23.0 °C | 19100 psi @Strain 1.75 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 133 MPa @Strain 3.24 %, Temperature 40.0 °C | 19300 psi @Strain 3.24 %, Temperature 104 °F | DAM; ISO 527 | |||
| 135 MPa @Strain 3.60 %, Temperature 40.0 °C | 19600 psi @Strain 3.60 %, Temperature 104 °F | DAM; Break; ISO 527 | |||
| 139 MPa @Strain 2.97 %, Temperature 0.000 °C | 20200 psi @Strain 2.97 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 140 MPa @Strain 2.00 %, Temperature 23.0 °C | 20300 psi @Strain 2.00 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 142 MPa @Strain 2.16 %, Temperature -20.0 °C | 20600 psi @Strain 2.16 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 145 MPa @Strain 3.30 %, Temperature 0.000 °C | 21000 psi @Strain 3.30 %, Temperature 32.0 °F | 50%RH; Break; ISO 527 | |||
| 147 MPa @Strain 2.25 %, Temperature 23.0 °C | 21300 psi @Strain 2.25 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 153 MPa @Strain 2.43 %, Temperature -20.0 °C | 22200 psi @Strain 2.43 %, Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 155 MPa @Strain 2.50 %, Temperature 23.0 °C | 22500 psi @Strain 2.50 %, Temperature 73.4 °F | DAM; Break; ISO 527 | |||
| 163 MPa @Strain 2.70 %, Temperature -20.0 °C | 23600 psi @Strain 2.70 %, Temperature -4.00 °F | 50%RH; Break; ISO 527 | |||
| Elongation at Break | 2.9 % @Temperature 23.0 °C | 2.9 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 7.0 % @Temperature 23.0 °C | 7.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 5.00 GPa @Temperature 23.0 °C | 725 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 7.30 GPa @Temperature 23.0 °C | 1060 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 210 MPa @Temperature 23.0 °C | 30500 psi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Shear Modulus | 0.333 GPa @Temperature 250 °C | 48.3 ksi @Temperature 482 °F | DAM; ISO 6721 | ||
| 0.403 GPa @Temperature 240 °C | 58.5 ksi @Temperature 464 °F | DAM; ISO 6721 | |||
| 0.441 GPa @Temperature 230 °C | 64.0 ksi @Temperature 446 °F | DAM; ISO 6721 | |||
| 0.464 GPa @Temperature 220 °C | 67.3 ksi @Temperature 428 °F | DAM; ISO 6721 | |||
| 0.479 GPa @Temperature 210 °C | 69.5 ksi @Temperature 410 °F | DAM; ISO 6721 | |||
| 0.491 GPa @Temperature 200 °C | 71.2 ksi @Temperature 392 °F | DAM; ISO 6721 | |||
| 0.502 GPa @Temperature 190 °C | 72.8 ksi @Temperature 374 °F | DAM; ISO 6721 | |||
| 0.513 GPa @Temperature 180 °C | 74.4 ksi @Temperature 356 °F | DAM; ISO 6721 | |||
| 0.522 GPa @Temperature 170 °C | 75.7 ksi @Temperature 338 °F | DAM; ISO 6721 | |||
| 0.531 GPa @Temperature 160 °C | 77.0 ksi @Temperature 320 °F | DAM; ISO 6721 | |||
| 0.540 GPa @Temperature 150 °C | 78.3 ksi @Temperature 302 °F | DAM; ISO 6721 | |||
| 0.549 GPa @Temperature 140 °C | 79.6 ksi @Temperature 284 °F | DAM; ISO 6721 | |||
| 0.558 GPa @Temperature 130 °C | 80.9 ksi @Temperature 266 °F | DAM; ISO 6721 | |||
| 0.570 GPa @Temperature 120 °C | 82.7 ksi @Temperature 248 °F | DAM; ISO 6721 | |||
| 0.587 GPa @Temperature 110 °C | 85.1 ksi @Temperature 230 °F | DAM; ISO 6721 | |||
| 0.614 GPa @Temperature 100 °C | 89.1 ksi @Temperature 212 °F | DAM; ISO 6721 | |||
| 0.659 GPa @Temperature 90.0 °C | 95.6 ksi @Temperature 194 °F | DAM; ISO 6721 | |||
| 0.730 GPa @Temperature 80.0 °C | 106 ksi @Temperature 176 °F | DAM; ISO 6721 | |||
| 0.841 GPa @Temperature 70.0 °C | 122 ksi @Temperature 158 °F | DAM; ISO 6721 | |||
| 1.015 GPa @Temperature 60.0 °C | 147.2 ksi @Temperature 140 °F | DAM; ISO 6721 | |||
| 1.28 GPa @Temperature 50.0 °C | 186 ksi @Temperature 122 °F | DAM; ISO 6721 | |||
| 1.424 GPa @Temperature 40.0 °C | 206.5 ksi @Temperature 104 °F | DAM; ISO 6721 | |||
| 1.509 GPa @Temperature 30.0 °C | 218.9 ksi @Temperature 86.0 °F | DAM; ISO 6721 | |||
| 1.564 GPa @Temperature 20.0 °C | 226.8 ksi @Temperature 68.0 °F | DAM; ISO 6721 | |||
| 1.606 GPa @Temperature 10.0 °C | 232.9 ksi @Temperature 50.0 °F | DAM; ISO 6721 | |||
| 1.63 GPa @Temperature 0.000 °C | 236 ksi @Temperature 32.0 °F | DAM; ISO 6721 | |||
| 1.643 GPa @Temperature -10.0 °C | 238.3 ksi @Temperature 14.0 °F | DAM; ISO 6721 | |||
| 1.653 GPa @Temperature -20.0 °C | 239.8 ksi @Temperature -4.00 °F | DAM; ISO 6721 | |||
| 1.67 GPa @Temperature -30.0 °C | 242 ksi @Temperature -22.0 °F | DAM; ISO 6721 | |||
| 1.699 GPa @Temperature -40.0 °C | 246.4 ksi @Temperature -40.0 °F | DAM; ISO 6721 | |||
| 1.745 GPa @Temperature -50.0 °C | 253.1 ksi @Temperature -58.0 °F | DAM; ISO 6721 | |||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 0.950 J/cm² @Temperature 23.0 °C | 4.52 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 4700 MPa @Temperature 23.0 °C | 682000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 3100 MPa @Temperature 23.0 °C | 450000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 23.0 °C | 1.00e+11 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm @Temperature 23.0 °C | >= 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| >= 1.00e+17 ohm-cm @Temperature 23.0 °C | >= 1.00e+17 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm @Temperature 23.0 °C | 1.00e+12 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm @Temperature 23.0 °C | >= 1.00e+15 ohm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.9 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 4.4 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.4 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dissipation Factor | 0.016 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.016 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.070 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.070 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 111 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 111 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 125 °C @Thickness 0.710 mm | 257 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF20< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Resin Identification | PA66-GF20 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||