- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 1.33
- 弯曲模量 [MPa]: 5.17
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | DAM; ASTM D792 | ||
| Density | 1.39 g/cc | 0.0502 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 33 % | 33 % | DAM | ||
| Linear Mold Shrinkage, Flow | 0.0013 cm/cm @Thickness 2.00 mm | 0.0013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa @Temperature 23.0 °C | 18100 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 185 MPa @Temperature 23.0 °C | 26800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 117 MPa @Temperature 23.0 °C | 17000 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.08 GPa @Temperature 23.0 °C | 1030 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 10.0 GPa @Temperature 23.0 °C | 1450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 270 MPa @Temperature 23.0 °C | 39200 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 5.17 GPa @Temperature 23.0 °C | 750 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 8.90 GPa @Temperature 23.0 °C | 1290 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 9.30 GPa @Temperature 23.0 °C | 1350 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 1.33 J/cm @Temperature 23.0 °C | 2.49 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 1.60 J/cm @Temperature 23.0 °C | 3.00 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Unnotched | 13.85 J/cm @Temperature 23.0 °C | 25.95 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| 14.4 J/cm @Temperature 23.0 °C | 27.0 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -40.0 °C | 5.23 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 71.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 39.4 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 71.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 39.4 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 108 µm/m-°C @Temperature 23.0 - 55.0 °C | 60.0 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 108 µm/m-°C @Temperature 23.0 - 55.0 °C | 60.0 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 125 µm/m-°C @Temperature 55.0 - 160 °C | 69.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 125 µm/m-°C @Temperature 55.0 - 160 °C | 69.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 257 °C | 495 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | DAM; ISO 75-1/-2 | ||
| 225 °C | 437 °F | DAM; ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 255 °C | 491 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Gloss, High | DAM | |||
| Surface Finish, Good | DAM | ||||
| Weather Resistance, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66+PA6-GF33< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| UV Resistant/Weatherable Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66+PA6-GF33 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Automotive Interior Applications | DAM | ||||
| Parts, Engineering | DAM | ||||
| Parts, Machine/Mechanical | DAM | ||||