  4. DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66

DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66

DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.19
  • 缺口冲击强度: 6.0
  • 弯曲模量 [MPa]: 3.12
 
Physical PropertiesMetricEnglishComments
Density 1.19 g/cc0.0430 lb/in³DAM; ISO 1183
Filler Content 14 %14 %DAM
Linear Mold Shrinkage, Flow 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  72.0 MPa
@Temperature 23.0 °C		10400 psi
@Temperature 73.4 °F		50%RH; ISO 527
 110 MPa
@Temperature 23.0 °C		16000 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  2.26 MPa
@Strain 0.100 %,
Temperature 150 °C		328 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.32 MPa
@Strain 0.100 %,
Temperature 100 °C		336 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.52 MPa
@Strain 0.200 %,
Temperature 150 °C		656 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.72 MPa
@Strain 0.200 %,
Temperature 100 °C		685 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.88 MPa
@Strain 0.100 %,
Temperature 23.0 °C		708 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.13 MPa
@Strain 0.100 %,
Temperature -40.0 °C		744 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.61 MPa
@Strain 0.300 %,
Temperature 150 °C		959 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.91 MPa
@Strain 0.300 %,
Temperature 100 °C		1000 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.32 MPa
@Strain 0.400 %,
Temperature 150 °C		1210 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.64 MPa
@Strain 0.400 %,
Temperature 100 °C		1250 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.72 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1410 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 10.07 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1461 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.48 MPa
@Strain 0.500 %,
Temperature 150 °C		1520 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.13 MPa
@Strain 0.500 %,
Temperature 100 °C		1614 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.23 MPa
@Strain 0.600 %,
Temperature 150 °C		1774 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.09 MPa
@Strain 0.600 %,
Temperature 100 °C		1899 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.94 MPa
@Strain 0.700 %,
Temperature 150 °C		2022 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.52 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2106 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 14.91 MPa
@Strain 0.700 %,
Temperature 100 °C		2163 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.02 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2178 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 15.46 MPa
@Strain 0.800 %,
Temperature 150 °C		2242 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.78 MPa
@Strain 0.800 %,
Temperature 100 °C		2434 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.98 MPa
@Strain 0.900 %,
Temperature 150 °C		2463 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.41 MPa
@Strain 1.00 %,
Temperature 150 °C		2670 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.54 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2689 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 18.63 MPa
@Strain 0.900 %,
Temperature 100 °C		2702 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.1 MPa
@Strain 0.400 %,
Temperature -40.0 °C		2770 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 19.75 MPa
@Strain 1.10 %,
Temperature 150 °C		2865 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.37 MPa
@Strain 1.00 %,
Temperature 100 °C		2954 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.09 MPa
@Strain 1.20 %,
Temperature 150 °C		3059 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.02 MPa
@Strain 1.10 %,
Temperature 100 °C		3194 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.42 MPa
@Strain 1.30 %,
Temperature 150 °C		3252 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.58 MPa
@Strain 1.40 %,
Temperature 150 °C		3420 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.66 MPa
@Strain 1.20 %,
Temperature 100 °C		3432 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.06 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3490 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 24.61 MPa
@Strain 0.500 %,
Temperature -40.0 °C		3569 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 24.73 MPa
@Strain 1.50 %,
Temperature 150 °C		3587 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.23 MPa
@Strain 1.30 %,
Temperature 100 °C		3659 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.9 MPa
@Strain 1.60 %,
Temperature 150 °C		3760 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.0 MPa
@Strain 1.70 %,
Temperature 150 °C		3920 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.04 MPa
@Strain 1.40 %,
Temperature 100 °C		3922 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.01 MPa
@Strain 1.80 %,
Temperature 150 °C		4063 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.6 MPa
@Strain 1.50 %,
Temperature 100 °C		4150 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.68 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4160 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.95 MPa
@Strain 1.90 %,
Temperature 150 °C		4199 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.24 MPa
@Strain 0.600 %,
Temperature -40.0 °C		4241 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 29.91 MPa
@Strain 2.00 %,
Temperature 150 °C		4338 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.95 MPa
@Strain 1.60 %,
Temperature 100 °C		4344 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.84 MPa
@Strain 2.10 %,
Temperature 150 °C		4473 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.29 MPa
@Strain 1.70 %,
Temperature 100 °C		4538 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.69 MPa
@Strain 2.20 %,
Temperature 150 °C		4596 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.51 MPa
@Strain 2.30 %,
Temperature 150 °C		4715 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.62 MPa
@Strain 1.80 %,
Temperature 100 °C		4731 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.3 MPa
@Strain 2.40 %,
Temperature 150 °C		4830 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.37 MPa
@Strain 0.700 %,
Temperature 23.0 °C		4840 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.93 MPa
@Strain 1.90 %,
Temperature 100 °C		4921 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.06 MPa
@Strain 2.50 %,
Temperature 150 °C		4940 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.19 MPa
@Strain 0.700 %,
Temperature -40.0 °C		4959 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 34.77 MPa
@Strain 2.60 %,
Temperature 150 °C		5043 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.05 MPa
@Strain 2.00 %,
Temperature 100 °C		5084 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.46 MPa
@Strain 2.70 %,
Temperature 150 °C		5143 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.11 MPa
@Strain 2.80 %,
Temperature 150 °C		5237 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.21 MPa
@Strain 2.10 %,
Temperature 100 °C		5252 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.69 MPa
@Strain 2.90 %,
Temperature 150 °C		5321 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.19 MPa
@Strain 3.00 %,
Temperature 150 °C		5394 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 2.20 %,
Temperature 100 °C		5410 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.68 MPa
@Strain 3.10 %,
Temperature 150 °C		5465 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.07 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5522 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.18 MPa
@Strain 3.20 %,
Temperature 150 °C		5538 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.38 MPa
@Strain 2.30 %,
Temperature 100 °C		5567 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.52 MPa
@Strain 0.800 %,
Temperature -40.0 °C		5587 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 38.59 MPa
@Strain 3.30 %,
Temperature 150 °C		5597 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.04 MPa
@Strain 3.40 %,
Temperature 150 °C		5662 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.45 MPa
@Strain 3.50 %,
Temperature 150 °C		5722 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.47 MPa
@Strain 2.40 %,
Temperature 100 °C		5725 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.84 MPa
@Strain 3.60 %,
Temperature 150 °C		5778 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.23 MPa
@Strain 3.70 %,
Temperature 150 °C		5835 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.54 MPa
@Strain 3.80 %,
Temperature 150 °C		5880 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.54 MPa
@Strain 2.50 %,
Temperature 100 °C		5880 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.91 MPa
@Strain 3.90 %,
Temperature 150 °C		5934 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.27 MPa
@Strain 4.00 %,
Temperature 150 °C		5986 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.54 MPa
@Strain 2.60 %,
Temperature 100 °C		6025 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.57 MPa
@Strain 4.10 %,
Temperature 150 °C		6029 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.92 MPa
@Strain 4.20 %,
Temperature 150 °C		6080 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.19 MPa
@Strain 4.30 %,
Temperature 150 °C		6119 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.33 MPa
@Strain 0.900 %,
Temperature 23.0 °C		6139 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 42.46 MPa
@Strain 4.40 %,
Temperature 150 °C		6158 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.5 MPa
@Strain 2.70 %,
Temperature 100 °C		6160 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.74 MPa
@Strain 4.50 %,
Temperature 150 °C		6199 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.98 MPa
@Strain 4.60 %,
Temperature 150 °C		6234 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.26 MPa
@Strain 4.70 %,
Temperature 150 °C		6274 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.4 MPa
@Strain 0.900 %,
Temperature -40.0 °C		6290 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 43.41 MPa
@Strain 2.80 %,
Temperature 100 °C		6296 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.49 MPa
@Strain 4.80 %,
Temperature 150 °C		6308 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.72 MPa
@Strain 4.90 %,
Temperature 150 °C		6341 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.95 MPa
@Strain 5.00 %,
Temperature 150 °C		6374 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.3 MPa
@Strain 2.90 %,
Temperature 100 °C		6430 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.31 MPa
@Strain 6.00 %,
Temperature 150 °C		6572 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.71 MPa
@Strain 3.10 %,
Temperature 100 °C		6630 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.28 MPa
@Strain 3.20 %,
Temperature 100 °C		6712 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.82 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6791 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 46.89 MPa
@Strain 7.00 %,
Temperature 150 °C		6801 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.9 MPa
@Strain 3.30 %,
Temperature 100 °C		6800 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.43 MPa
@Strain 3.40 %,
Temperature 100 °C		6879 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.73 MPa
@Strain 8.00 %,
Temperature 150 °C		6923 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.94 MPa
@Strain 3.50 %,
Temperature 100 °C		6953 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.24 MPa
@Strain 1.00 %,
Temperature -40.0 °C		6997 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 48.32 MPa
@Strain 9.00 %,
Temperature 150 °C		7008 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.41 MPa
@Strain 3.60 %,
Temperature 100 °C		7021 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.69 MPa
@Strain 10.0 %,
Temperature 150 °C		7062 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.78 MPa
@Strain 11.0 %,
Temperature 150 °C		7075 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.9 MPa
@Strain 3.70 %,
Temperature 100 °C		7090 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.38 MPa
@Strain 3.80 %,
Temperature 100 °C		7162 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.79 MPa
@Strain 3.90 %,
Temperature 100 °C		7221 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.24 MPa
@Strain 4.00 %,
Temperature 100 °C		7287 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.59 MPa
@Strain 4.10 %,
Temperature 100 °C		7337 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.96 MPa
@Strain 4.20 %,
Temperature 100 °C		7391 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.06 MPa
@Strain 1.10 %,
Temperature 23.0 °C		7406 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 51.29 MPa
@Strain 4.30 %,
Temperature 100 °C		7439 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 4.40 %,
Temperature 100 °C		7480 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.93 MPa
@Strain 4.50 %,
Temperature 100 °C		7532 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.17 MPa
@Strain 4.60 %,
Temperature 100 °C		7567 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.47 MPa
@Strain 4.70 %,
Temperature 100 °C		7610 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.68 MPa
@Strain 4.80 %,
Temperature 100 °C		7641 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.92 MPa
@Strain 4.90 %,
Temperature 100 °C		7675 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.02 MPa
@Strain 1.10 %,
Temperature -40.0 °C		7690 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 53.12 MPa
@Strain 5.00 %,
Temperature 100 °C		7704 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.42 MPa
@Strain 6.00 %,
Temperature 100 °C		7893 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.16 MPa
@Strain 1.20 %,
Temperature 23.0 °C		8000 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 55.8 MPa
@Strain 7.00 %,
Temperature 100 °C		8090 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.45 MPa
@Strain 8.00 %,
Temperature 100 °C		8187 psi
@Strain 8.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.83 MPa
@Strain 9.00 %,
Temperature 100 °C		8243 psi
@Strain 9.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.94 MPa
@Strain 10.0 %,
Temperature 100 °C		8258 psi
@Strain 10.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.73 MPa
@Strain 1.20 %,
Temperature -40.0 °C		8373 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 59.21 MPa
@Strain 1.30 %,
Temperature 23.0 °C		8588 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.23 MPa
@Strain 1.30 %,
Temperature -40.0 °C		9026 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.18 MPa
@Strain 1.40 %,
Temperature 23.0 °C		9164 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.89 MPa
@Strain 1.40 %,
Temperature -40.0 °C		9702 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 67.0 MPa
@Strain 1.50 %,
Temperature 23.0 °C		9720 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 70.66 MPa
@Strain 1.60 %,
Temperature 23.0 °C		10250 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.33 MPa
@Strain 1.50 %,
Temperature -40.0 °C		10350 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 74.24 MPa
@Strain 1.70 %,
Temperature 23.0 °C		10770 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.67 MPa
@Strain 1.60 %,
Temperature -40.0 °C		10980 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 77.66 MPa
@Strain 1.80 %,
Temperature 23.0 °C		11260 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.92 MPa
@Strain 1.70 %,
Temperature -40.0 °C		11590 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.85 MPa
@Strain 1.90 %,
Temperature 23.0 °C		11730 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.85 MPa
@Strain 2.00 %,
Temperature 23.0 °C		12160 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.2 MPa
@Strain 1.80 %,
Temperature -40.0 °C		12200 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.73 MPa
@Strain 2.10 %,
Temperature 23.0 °C		12580 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.28 MPa
@Strain 1.90 %,
Temperature -40.0 °C		12800 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.39 MPa
@Strain 2.20 %,
Temperature 23.0 °C		12960 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 91.9 MPa
@Strain 2.30 %,
Temperature 23.0 °C		13300 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 92.31 MPa
@Strain 2.00 %,
Temperature -40.0 °C		13390 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.2 MPa
@Strain 2.40 %,
Temperature 23.0 °C		13700 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 96.17 MPa
@Strain 2.10 %,
Temperature -40.0 °C		13950 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.29 MPa
@Strain 2.50 %,
Temperature 23.0 °C		13970 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.3 MPa
@Strain 2.60 %,
Temperature 23.0 °C		14300 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 100.05 MPa
@Strain 2.20 %,
Temperature -40.0 °C		14511 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.12 MPa
@Strain 2.70 %,
Temperature 23.0 °C		14521 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 101.76 MPa
@Strain 2.80 %,
Temperature 23.0 °C		14759 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.29 MPa
@Strain 2.90 %,
Temperature 23.0 °C		14981 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.69 MPa
@Strain 2.30 %,
Temperature -40.0 °C		15039 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 104.61 MPa
@Strain 3.00 %,
Temperature 23.0 °C		15172 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 105.67 MPa
@Strain 3.10 %,
Temperature 23.0 °C		15326 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 106.66 MPa
@Strain 3.20 %,
Temperature 23.0 °C		15470 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.16 MPa
@Strain 2.40 %,
Temperature -40.0 °C		15542 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.56 MPa
@Strain 3.30 %,
Temperature 23.0 °C		15600 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 108.33 MPa
@Strain 3.40 %,
Temperature 23.0 °C		15712 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 108.91 MPa
@Strain 3.50 %,
Temperature 23.0 °C		15796 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 108.98 MPa
@Strain 3.80 %,
Temperature 23.0 °C		15806 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.29 MPa
@Strain 3.60 %,
Temperature 23.0 °C		15851 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.29 MPa
@Strain 3.70 %,
Temperature 23.0 °C		15851 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 110.54 MPa
@Strain 2.50 %,
Temperature -40.0 °C		16033 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.93 MPa
@Strain 2.60 %,
Temperature -40.0 °C		16524 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.14 MPa
@Strain 2.70 %,
Temperature -40.0 °C		16990 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 120.19 MPa
@Strain 2.80 %,
Temperature -40.0 °C		17432 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.14 MPa
@Strain 2.90 %,
Temperature -40.0 °C		17860 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.6 MPa
@Strain 3.00 %,
Temperature -40.0 °C		18220 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 127.71 MPa
@Strain 3.10 %,
Temperature -40.0 °C		18523 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 129.67 MPa
@Strain 3.20 %,
Temperature -40.0 °C		18807 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 131.61 MPa
@Strain 3.30 %,
Temperature -40.0 °C		19088 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 133.45 MPa
@Strain 3.40 %,
Temperature -40.0 °C		19355 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 135.35 MPa
@Strain 3.50 %,
Temperature -40.0 °C		19631 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137.14 MPa
@Strain 3.60 %,
Temperature -40.0 °C		19891 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 138.94 MPa
@Strain 3.70 %,
Temperature -40.0 °C		20152 psi
@Strain 3.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.77 MPa
@Strain 3.80 %,
Temperature -40.0 °C		20417 psi
@Strain 3.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 142.48 MPa
@Strain 3.90 %,
Temperature -40.0 °C		20665 psi
@Strain 3.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 144.17 MPa
@Strain 4.00 %,
Temperature -40.0 °C		20910 psi
@Strain 4.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 145.8 MPa
@Strain 4.10 %,
Temperature -40.0 °C		21150 psi
@Strain 4.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 147.39 MPa
@Strain 4.20 %,
Temperature -40.0 °C		21377 psi
@Strain 4.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 148.49 MPa
@Strain 4.30 %,
Temperature -40.0 °C		21537 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.8 %
@Temperature 23.0 °C		3.8 %
@Temperature 73.4 °F		DAM; ISO 527
 9.0 %
@Temperature 23.0 °C		9.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  3.30 GPa
@Temperature 23.0 °C		479 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.00 GPa
@Temperature 23.0 °C		725 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  3.12 GPa
@Temperature 23.0 °C		453 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.40 GPa
@Temperature 23.0 °C		638 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched (ISO)  6.00 kJ/m²
@Temperature -40.0 °C		2.86 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature 0.000 °C		5.23 ft-lb/in²
@Temperature 32.0 °F		DAM; ISO 180/1A
 13.0 kJ/m²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Charpy Impact Unnotched  7.10 J/cm²
@Temperature -30.0 °C		33.8 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 7.30 J/cm²
@Temperature 23.0 °C		34.7 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 7.60 J/cm²
@Temperature 23.0 °C		36.2 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm²
@Temperature -40.0 °C		2.86 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 0.700 J/cm²
@Temperature -30.0 °C		3.33 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.900 J/cm²
@Temperature -30.0 °C		4.28 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.70 J/cm²
@Temperature 23.0 °C		8.09 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Dissipation Factor  0.018
@Frequency 100 Hz,
Temperature 23.0 °C		0.018
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.027
@Frequency 100 Hz,
Temperature 23.0 °C		0.027
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 240 °C464 °FDAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 50.0 - 100 °C122 - 212 °FDAM
 80.0 °C176 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
FeaturesChemical Resistance, GoodDAM
 Fatigue ResistantDAM
 Fuel ResistantDAM
 Grease ResistantDAM
 Heat Aging Resistance, GoodDAM
 Heat StabilizedDAM
 Impact ModifiedDAM
 Impact Resistance, GoodDAM
 Oil ResistantDAM
 Thermal Aging Resistance, GoodDAM
 Toughness, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA66-IGF14<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
 Toughened ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-IGF14ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45487.html

免责声明: 本文 DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4