  3. PA66
  4. DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66

DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66

DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.32
  • 吸水率 [%]: 0.83
  • 成型收缩率 [%]: 0.004
  • 缺口冲击强度: 2.19
  • 弯曲模量 [MPa]: 5.07
  • 热变形温度 [℃]: 262.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.33 g/cc1.33 g/ccDAM; ASTM D792
Density 1.32 g/cc0.0477 lb/in³DAM; ISO 1183
Filler Content 33 %33 %DAM
Water Absorption 0.83 %
@Temperature 23.0 °C		0.83 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0040 cm/cm
@Thickness 3.20 mm		0.0040 in/in
@Thickness 0.126 in		Flow; DAM
 0.012 cm/cm
@Thickness 3.20 mm		0.012 in/in
@Thickness 0.126 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  95.0 MPa
@Temperature 23.0 °C		13800 psi
@Temperature 73.4 °F		50%RH; ISO 527
 142 MPa
@Temperature 23.0 °C		20600 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  110 MPa
@Temperature 23.0 °C		16000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 145 MPa
@Temperature 23.0 °C		21000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  5.976 MPa
@Strain 0.100 %,
Temperature 23.0 °C		866.7 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 527
 15.138 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2195.6 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 527
 19.0 MPa
@Strain 3.92 %,
Temperature 40.0 °C		2760 psi
@Strain 3.92 %,
Temperature 104 °F		DAM; ISO 527
 19.18 MPa
@Strain 0.620 %,
Temperature 120 °C		2782 psi
@Strain 0.620 %,
Temperature 248 °F		50%RH; ISO 527
 21.03 MPa
@Strain 0.660 %,
Temperature 120 °C		3050 psi
@Strain 0.660 %,
Temperature 248 °F		DAM; ISO 527
 21.14 MPa
@Strain 0.600 %,
Temperature 90.0 °C		3066 psi
@Strain 0.600 %,
Temperature 194 °F		50%RH; ISO 527
 22.6 MPa
@Strain 0.590 %,
Temperature 60.0 °C		3280 psi
@Strain 0.590 %,
Temperature 140 °F		50%RH; ISO 527
 22.743 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3298.6 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 527
 24.19 MPa
@Strain 0.680 %,
Temperature 90.0 °C		3508 psi
@Strain 0.680 %,
Temperature 194 °F		DAM; ISO 527
 27.72 MPa
@Strain 0.630 %,
Temperature 40.0 °C		4020 psi
@Strain 0.630 %,
Temperature 104 °F		50%RH; ISO 527
 29.196 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4234.5 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 527
 30.07 MPa
@Strain 0.400 %,
Temperature 40.0 °C		4361 psi
@Strain 0.400 %,
Temperature 104 °F		DAM; ISO 527
 30.46 MPa
@Strain 0.580 %,
Temperature 60.0 °C		4418 psi
@Strain 0.580 %,
Temperature 140 °F		DAM; ISO 527
 30.73 MPa
@Strain 1.14 %,
Temperature 120 °C		4457 psi
@Strain 1.14 %,
Temperature 248 °F		50%RH; ISO 527
 32.25 MPa
@Strain 0.570 %,
Temperature 23.0 °C		4677 psi
@Strain 0.570 %,
Temperature 73.4 °F		50%RH; ISO 527
 34.19 MPa
@Strain 1.11 %,
Temperature 90.0 °C		4959 psi
@Strain 1.11 %,
Temperature 194 °F		50%RH; ISO 527
 35.86 MPa
@Strain 1.36 %,
Temperature 120 °C		5201 psi
@Strain 1.36 %,
Temperature 248 °F		DAM; ISO 527
 37.39 MPa
@Strain 1.09 %,
Temperature 60.0 °C		5423 psi
@Strain 1.09 %,
Temperature 140 °F		50%RH; ISO 527
 37.395 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5423.7 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 527
 39.45 MPa
@Strain 1.73 %,
Temperature 120 °C		5722 psi
@Strain 1.73 %,
Temperature 248 °F		50%RH; ISO 527
 40.47 MPa
@Strain 1.33 %,
Temperature 90.0 °C		5870 psi
@Strain 1.33 %,
Temperature 194 °F		DAM; ISO 527
 43.893 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6366.2 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 527
 44.58 MPa
@Strain 1.98 %,
Temperature 120 °C		6466 psi
@Strain 1.98 %,
Temperature 248 °F		DAM; ISO 527
 44.7 MPa
@Strain 1.68 %,
Temperature 90.0 °C		6480 psi
@Strain 1.68 %,
Temperature 194 °F		50%RH; ISO 527
 44.8 MPa
@Strain 2.26 %,
Temperature 120 °C		6500 psi
@Strain 2.26 %,
Temperature 248 °F		50%RH; ISO 527
 46.77 MPa
@Strain 1.22 %,
Temperature 40.0 °C		6783 psi
@Strain 1.22 %,
Temperature 104 °F		50%RH; ISO 527
 49.02 MPa
@Strain 2.85 %,
Temperature 120 °C		7110 psi
@Strain 2.85 %,
Temperature 248 °F		50%RH; ISO 527
 49.88 MPa
@Strain 1.65 %,
Temperature 60.0 °C		7234 psi
@Strain 1.65 %,
Temperature 140 °F		50%RH; ISO 527
 50.706 MPa
@Strain 0.700 %,
Temperature 23.0 °C		7354.3 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 527
 51.03 MPa
@Strain 1.11 %,
Temperature 60.0 °C		7401 psi
@Strain 1.11 %,
Temperature 140 °F		DAM; ISO 527
 51.6 MPa
@Strain 2.68 %,
Temperature 120 °C		7480 psi
@Strain 2.68 %,
Temperature 248 °F		DAM; ISO 527
 51.63 MPa
@Strain 3.37 %,
Temperature 120 °C		7488 psi
@Strain 3.37 %,
Temperature 248 °F		50%RH; ISO 527
 52.19 MPa
@Strain 2.24 %,
Temperature 90.0 °C		7570 psi
@Strain 2.24 %,
Temperature 194 °F		50%RH; ISO 527
 53.29 MPa
@Strain 2.04 %,
Temperature 90.0 °C		7729 psi
@Strain 2.04 %,
Temperature 194 °F		DAM; ISO 527
 53.79 MPa
@Strain 3.96 %,
Temperature 120 °C		7802 psi
@Strain 3.96 %,
Temperature 248 °F		50%RH; ISO 527
 54.45 MPa
@Strain 1.09 %,
Temperature 23.0 °C		7897 psi
@Strain 1.09 %,
Temperature 73.4 °F		50%RH; ISO 527
 55.07 MPa
@Strain 4.48 %,
Temperature 120 °C		7987 psi
@Strain 4.48 %,
Temperature 248 °F		50%RH; ISO 527
 55.63 MPa
@Strain 5.66 %,
Temperature 120 °C		8068 psi
@Strain 5.66 %,
Temperature 248 °F		50%RH; ISO 527
 55.86 MPa
@Strain 3.30 %,
Temperature 120 °C		8102 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 527
 55.89 MPa
@Strain 5.07 %,
Temperature 120 °C		8106 psi
@Strain 5.07 %,
Temperature 248 °F		50%RH; ISO 527
 57.09 MPa
@Strain 2.81 %,
Temperature 90.0 °C		8280 psi
@Strain 2.81 %,
Temperature 194 °F		50%RH; ISO 527
 57.33 MPa
@Strain 0.800 %,
Temperature 23.0 °C		8315 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 527
 58.13 MPa
@Strain 0.830 %,
Temperature 40.0 °C		8431 psi
@Strain 0.830 %,
Temperature 104 °F		DAM; ISO 527
 58.96 MPa
@Strain 3.92 %,
Temperature 120 °C		8551 psi
@Strain 3.92 %,
Temperature 248 °F		DAM; ISO 527
 58.97 MPa
@Strain 2.21 %,
Temperature 60.0 °C		8553 psi
@Strain 2.21 %,
Temperature 140 °F		50%RH; ISO 527
 60.13 MPa
@Strain 3.32 %,
Temperature 90.0 °C		8721 psi
@Strain 3.32 %,
Temperature 194 °F		50%RH; ISO 527
 60.78 MPa
@Strain 1.81 %,
Temperature 40.0 °C		8815 psi
@Strain 1.81 %,
Temperature 104 °F		50%RH; ISO 527
 61.57 MPa
@Strain 2.69 %,
Temperature 90.0 °C		8930 psi
@Strain 2.69 %,
Temperature 194 °F		DAM; ISO 527
 61.63 MPa
@Strain 4.62 %,
Temperature 120 °C		8939 psi
@Strain 4.62 %,
Temperature 248 °F		DAM; ISO 527
 62.48 MPa
@Strain 3.89 %,
Temperature 90.0 °C		9062 psi
@Strain 3.89 %,
Temperature 194 °F		50%RH; ISO 527
 63.23 MPa
@Strain 5.24 %,
Temperature 120 °C		9171 psi
@Strain 5.24 %,
Temperature 248 °F		DAM; ISO 527
 63.594 MPa
@Strain 0.900 %,
Temperature 23.0 °C		9223.5 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 527
 63.84 MPa
@Strain 5.53 %,
Temperature 90.0 °C		9259 psi
@Strain 5.53 %,
Temperature 194 °F		50%RH; ISO 527
 64.02 MPa
@Strain 4.46 %,
Temperature 90.0 °C		9285 psi
@Strain 4.46 %,
Temperature 194 °F		50%RH; ISO 527
 64.24 MPa
@Strain 5.85 %,
Temperature 120 °C		9317 psi
@Strain 5.85 %,
Temperature 248 °F		DAM; ISO 527
 64.71 MPa
@Strain 4.96 %,
Temperature 90.0 °C		9385 psi
@Strain 4.96 %,
Temperature 194 °F		50%RH; ISO 527
 64.83 MPa
@Strain 2.71 %,
Temperature 60.0 °C		9403 psi
@Strain 2.71 %,
Temperature 140 °F		50%RH; ISO 527
 65.3 MPa
@Strain 6.56 %,
Temperature 120 °C		9470 psi
@Strain 6.56 %,
Temperature 248 °F		DAM; ISO 527
 65.75 MPa
@Strain 1.65 %,
Temperature 60.0 °C		9536 psi
@Strain 1.65 %,
Temperature 140 °F		DAM; ISO 527
 67.27 MPa
@Strain 3.34 %,
Temperature 90.0 °C		9757 psi
@Strain 3.34 %,
Temperature 194 °F		DAM; ISO 527
 69.34 MPa
@Strain 3.27 %,
Temperature 60.0 °C		10060 psi
@Strain 3.27 %,
Temperature 140 °F		50%RH; ISO 527
 69.552 MPa
@Strain 1.00 %,
Temperature 23.0 °C		10088 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 527
 70.43 MPa
@Strain 1.61 %,
Temperature 23.0 °C		10220 psi
@Strain 1.61 %,
Temperature 73.4 °F		50%RH; ISO 527
 70.96 MPa
@Strain 2.40 %,
Temperature 40.0 °C		10290 psi
@Strain 2.40 %,
Temperature 104 °F		50%RH; ISO 527
 71.19 MPa
@Strain 3.98 %,
Temperature 90.0 °C		10330 psi
@Strain 3.98 %,
Temperature 194 °F		DAM; ISO 527
 72.29 MPa
@Strain 3.83 %,
Temperature 60.0 °C		10480 psi
@Strain 3.83 %,
Temperature 140 °F		50%RH; ISO 527
 73.93 MPa
@Strain 4.63 %,
Temperature 90.0 °C		10720 psi
@Strain 4.63 %,
Temperature 194 °F		DAM; ISO 527
 74.04 MPa
@Strain 4.33 %,
Temperature 60.0 °C		10740 psi
@Strain 4.33 %,
Temperature 140 °F		50%RH; ISO 527
 74.91 MPa
@Strain 2.09 %,
Temperature 60.0 °C		10860 psi
@Strain 2.09 %,
Temperature 140 °F		DAM; ISO 527
 75.114 MPa
@Strain 1.10 %,
Temperature 23.0 °C		10894 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 527
 75.14 MPa
@Strain 4.89 %,
Temperature 60.0 °C		10900 psi
@Strain 4.89 %,
Temperature 140 °F		50%RH; ISO 527
 75.21 MPa
@Strain 5.45 %,
Temperature 60.0 °C		10910 psi
@Strain 5.45 %,
Temperature 140 °F		50%RH; ISO 527
 75.71 MPa
@Strain 5.34 %,
Temperature 90.0 °C		10980 psi
@Strain 5.34 %,
Temperature 194 °F		DAM; ISO 527
 75.92 MPa
@Strain 6.64 %,
Temperature 90.0 °C		11010 psi
@Strain 6.64 %,
Temperature 194 °F		DAM; ISO 527
 76.5 MPa
@Strain 5.99 %,
Temperature 90.0 °C		11100 psi
@Strain 5.99 %,
Temperature 194 °F		DAM; ISO 527
 76.92 MPa
@Strain 1.20 %,
Temperature 40.0 °C		11160 psi
@Strain 1.20 %,
Temperature 104 °F		DAM; ISO 527
 77.83 MPa
@Strain 2.99 %,
Temperature 40.0 °C		11290 psi
@Strain 2.99 %,
Temperature 104 °F		50%RH; ISO 527
 80.397 MPa
@Strain 1.20 %,
Temperature 23.0 °C		11661 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 527
 82.31 MPa
@Strain 3.58 %,
Temperature 40.0 °C		11940 psi
@Strain 3.58 %,
Temperature 104 °F		50%RH; ISO 527
 82.81 MPa
@Strain 2.13 %,
Temperature 23.0 °C		12010 psi
@Strain 2.13 %,
Temperature 73.4 °F		50%RH; ISO 527
 83.42 MPa
@Strain 2.63 %,
Temperature 60.0 °C		12100 psi
@Strain 2.63 %,
Temperature 140 °F		DAM; ISO 527
 85.05 MPa
@Strain 4.18 %,
Temperature 40.0 °C		12340 psi
@Strain 4.18 %,
Temperature 104 °F		50%RH; ISO 527
 85.545 MPa
@Strain 1.30 %,
Temperature 23.0 °C		12407 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 527
 86.51 MPa
@Strain 4.77 %,
Temperature 40.0 °C		12550 psi
@Strain 4.77 %,
Temperature 104 °F		50%RH; ISO 527
 86.59 MPa
@Strain 5.95 %,
Temperature 40.0 °C		12560 psi
@Strain 5.95 %,
Temperature 104 °F		50%RH; ISO 527
 87.01 MPa
@Strain 5.36 %,
Temperature 40.0 °C		12620 psi
@Strain 5.36 %,
Temperature 104 °F		50%RH; ISO 527
 89.15 MPa
@Strain 3.16 %,
Temperature 60.0 °C		12930 psi
@Strain 3.16 %,
Temperature 140 °F		DAM; ISO 527
 90.189 MPa
@Strain 1.40 %,
Temperature 23.0 °C		13081 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 527
 91.14 MPa
@Strain 1.57 %,
Temperature 40.0 °C		13220 psi
@Strain 1.57 %,
Temperature 104 °F		DAM; ISO 527
 91.27 MPa
@Strain 2.65 %,
Temperature 23.0 °C		13240 psi
@Strain 2.65 %,
Temperature 73.4 °F		50%RH; ISO 527
 92.6 MPa
@Strain 3.70 %,
Temperature 60.0 °C		13400 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 527
 94.437 MPa
@Strain 1.50 %,
Temperature 23.0 °C		13697 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 527
 94.66 MPa
@Strain 4.23 %,
Temperature 60.0 °C		13730 psi
@Strain 4.23 %,
Temperature 140 °F		DAM; ISO 527
 95.52 MPa
@Strain 5.21 %,
Temperature 60.0 °C		13850 psi
@Strain 5.21 %,
Temperature 140 °F		DAM; ISO 527
 95.58 MPa
@Strain 4.77 %,
Temperature 60.0 °C		13860 psi
@Strain 4.77 %,
Temperature 140 °F		DAM; ISO 527
 96.7 MPa
@Strain 3.18 %,
Temperature 23.0 °C		14000 psi
@Strain 3.18 %,
Temperature 73.4 °F		50%RH; ISO 527
 98.55 MPa
@Strain 1.60 %,
Temperature 23.0 °C		14290 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 527
 100.16 MPa
@Strain 3.70 %,
Temperature 23.0 °C		14527 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 527
 101.73 MPa
@Strain 5.26 %,
Temperature 23.0 °C		14755 psi
@Strain 5.26 %,
Temperature 73.4 °F		50%RH; ISO 527
 101.83 MPa
@Strain 4.22 %,
Temperature 23.0 °C		14769 psi
@Strain 4.22 %,
Temperature 73.4 °F		50%RH; ISO 527
 102.34 MPa
@Strain 4.74 %,
Temperature 23.0 °C		14843 psi
@Strain 4.74 %,
Temperature 73.4 °F		50%RH; ISO 527
 102.36 MPa
@Strain 1.70 %,
Temperature 23.0 °C		14846 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 527
 103.41 MPa
@Strain 2.00 %,
Temperature 40.0 °C		14998 psi
@Strain 2.00 %,
Temperature 104 °F		DAM; ISO 527
 105.73 MPa
@Strain 1.80 %,
Temperature 23.0 °C		15335 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 527
 108.82 MPa
@Strain 1.90 %,
Temperature 23.0 °C		15783 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 527
 110.55 MPa
@Strain 2.37 %,
Temperature 40.0 °C		16034 psi
@Strain 2.37 %,
Temperature 104 °F		DAM; ISO 527
 111.74 MPa
@Strain 2.00 %,
Temperature 23.0 °C		16207 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 527
 114.49 MPa
@Strain 2.10 %,
Temperature 23.0 °C		16605 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 527
 115.12 MPa
@Strain 2.74 %,
Temperature 40.0 °C		16697 psi
@Strain 2.74 %,
Temperature 104 °F		DAM; ISO 527
 116.95 MPa
@Strain 2.20 %,
Temperature 23.0 °C		16962 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 527
 117.9 MPa
@Strain 3.17 %,
Temperature 40.0 °C		17100 psi
@Strain 3.17 %,
Temperature 104 °F		DAM; ISO 527
 118.7 MPa
@Strain 3.54 %,
Temperature 40.0 °C		17220 psi
@Strain 3.54 %,
Temperature 104 °F		DAM; ISO 527
 119.29 MPa
@Strain 2.30 %,
Temperature 23.0 °C		17302 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 527
 121.45 MPa
@Strain 2.40 %,
Temperature 23.0 °C		17615 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 527
 123.44 MPa
@Strain 2.50 %,
Temperature 23.0 °C		17903 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 527
 125.24 MPa
@Strain 2.60 %,
Temperature 23.0 °C		18165 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 527
 126.95 MPa
@Strain 2.70 %,
Temperature 23.0 °C		18413 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 527
 128.47 MPa
@Strain 2.80 %,
Temperature 23.0 °C		18633 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 527
 129.84 MPa
@Strain 2.90 %,
Temperature 23.0 °C		18832 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 527
 131.09 MPa
@Strain 3.00 %,
Temperature 23.0 °C		19013 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 527
 132.32 MPa
@Strain 3.10 %,
Temperature 23.0 °C		19191 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 527
 133.24 MPa
@Strain 3.20 %,
Temperature 23.0 °C		19325 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 527
 134.06 MPa
@Strain 3.30 %,
Temperature 23.0 °C		19444 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 527
 134.87 MPa
@Strain 3.40 %,
Temperature 23.0 °C		19561 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 527
 135.49 MPa
@Strain 3.50 %,
Temperature 23.0 °C		19651 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 527
Elongation at Break  4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		DAM; ISO 527
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  5.80 GPa
@Temperature 23.0 °C		841 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 8.70 GPa
@Temperature 23.0 °C		1260 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 205 MPa
@Temperature 23.0 °C		29700 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  5.07 GPa
@Temperature 23.0 °C		735 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 5.20 GPa
@Temperature 23.0 °C		754 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 6.90 GPa
@Temperature 23.0 °C		1000 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 7.40 GPa
@Temperature 23.0 °C		1070 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched  2.19 J/cm
@Temperature 23.0 °C		4.10 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 2.35 J/cm
@Temperature 23.0 °C		4.40 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched 13.35 J/cm
@Temperature 23.0 °C		25.01 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 10.0 kJ/m²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 14.0 kJ/m²
@Temperature -30.0 °C		6.66 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 15.0 kJ/m²
@Temperature -40.0 °C		7.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 20.0 kJ/m²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
 21.0 kJ/m²
@Temperature 23.0 °C		9.99 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  74.0 kJ/m²
@Temperature 23.0 °C		35.2 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 75.0 kJ/m²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 80.0 kJ/m²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 80.0 kJ/m²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  7.50 J/cm²
@Temperature -30.0 °C		35.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.00 J/cm²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 9.10 J/cm²
@Temperature 23.0 °C		43.3 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  1.30 J/cm²
@Temperature -40.0 °C		6.19 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.30 J/cm²
@Temperature -40.0 °C		6.19 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 1.40 J/cm²
@Temperature -30.0 °C		6.66 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 1.40 J/cm²
@Temperature -30.0 °C		6.66 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 2.00 J/cm²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 2.20 J/cm²
@Temperature 23.0 °C		10.5 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index  400 - 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		400 - 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 96.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		53.3 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 119 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 119 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 130 µm/m-°C
@Temperature 55.0 - 160 °C		72.2 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 130 µm/m-°C
@Temperature 55.0 - 160 °C		72.2 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 262 °C504 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 247 °C477 °FDAM; ISO 75-1/-2
 250 °C482 °FDAM; ASTM D648
UL RTI, Electrical  120 °C
@Thickness 0.750 mm		248 °F
@Thickness 0.0295 in		DAM; UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
 105 °C
@Thickness 1.50 mm		221 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  85.0 °C
@Thickness 0.750 mm		185 °F
@Thickness 0.0295 in		DAM; UL 746B
 95.0 °C
@Thickness 1.50 mm		203 °F
@Thickness 0.0591 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 23 %23 %DAM; ISO 4589-1/-2
Glow Wire Test  650 °C
@Thickness 0.750 mm		1200 °F
@Thickness 0.0295 in		DAM; IEC 60695-2-12
 650 °C
@Thickness 1.50 mm		1200 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 675 °C
@Thickness 1.50 mm		1250 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 675 °C
@Thickness 0.750 mm		1250 °F
@Thickness 0.0295 in		DAM; Ignition; IEC 60695-2-13
 725 °C
@Thickness 3.00 mm		1340 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 775 °C
@Thickness 3.00 mm		1430 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 50.0 - 100 °C122 - 212 °FDAM
 80.0 °C176 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveImpact ModifierDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesImpact Resistance, HighDAM
 LubricatedDAM
 Toughness, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-IGF33<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
 Toughened ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-IGF33ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 FastenersDAM
 Industrial ApplicationsDAM
 Sporting GoodsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45494.html

免责声明: 本文 DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4