- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.2
- 缺口冲击强度: 2.14
- 弯曲模量 [MPa]: 0.896
- 硬度: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 46.2 MPa | 6700 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Strength | 34.5 MPa | 5000 psi | ASTM D790 |
| Flexural Modulus | 0.896 GPa | 130 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | 73°F; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.8 @Frequency 100 Hz | 5.8 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| HB | HB | 0.118 in, BK | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |