- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 0.8
- 缺口冲击强度: 8.54
- 弯曲模量 [MPa]: 1.79
- 硬度: 107.0
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.80 % | 0.80 % | 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | 0.125 in; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 107 | 107 | ASTM D785 | ||
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 | ||
| Elongation at Break | 55 % | 55 % | ASTM D638 | ||
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 | ||
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 | ||
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | 73°F; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C | 78.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 | ||
| Flammability, UL94 | HB | HB | 0.0590 in, NC | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |||
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |||
| Drying Temperature | 73.9 °C | 165 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.18 % | 0.18 % | |||
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |||
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |||
| Descriptive Properties | |||||
| Holding Pressure | 400 to 1400 psi | ||||
| Injection Rate | Fast | ||||