- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.2
- 缺口冲击强度: 1.6
- 弯曲模量 [MPa]: 2.21
- 硬度: 114.0
- 热变形温度 [℃]: 229.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 | ||
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125 in; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 114 | 114 | ASTM D785 | ||
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 | ||
| Elongation at Break | 40 % | 40 % | ASTM D638 | ||
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 | ||
| Flexural Modulus | 2.21 GPa | 320 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | 73°F; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.5 @Frequency 100 Hz | 3.5 @Frequency 100 Hz | ASTM D150 | ||
| Dielectric Strength | 21.3 kV/mm | 540 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 113 µm/m-°C @Temperature 20.0 °C | 63.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 445 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 | ||
| Flammability, UL94 | HB | HB | 0.0590 in, BK | ||
| HB | HB | 0.118 in, BK | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |||
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |||
| Drying Temperature | 73.9 °C | 165 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.18 % | 0.18 % | |||
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |||
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |||
| Descriptive Properties | |||||
| Holding Pressure | 400 to 1400 psi | ||||
| Injection Rate | Fast | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.