| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 73.5 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 228 °C | 442 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |