- 吸水率 [%]: 0.7
- 缺口冲击强度: 2.65
- 弯曲模量 [MPa]: 11.772
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec | 0.70 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm | 0.0035 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 220.725 MPa | 32013.5 psi | ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| Flexural Strength | 323.73 MPa | 46953 psi | ASTM D790 |
| Flexural Modulus | 11.772 GPa | 1707.4 ksi | ASTM D790 |
| Izod Impact, Notched | 2.65 J/cm @Temperature 23.0 °C | 4.96 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 2.65 J/cm @Temperature -30.0 °C | 4.96 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |