- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.29
- 拉伸强度 [MPa]: 51.7
- 断裂伸长率 [%]: 13.8
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 0.0343
- 硬度: 100.0
- 热变形温度 [℃]: 188.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 - 1.67 g/cc | 0.0385 - 0.0603 lb/in³ | Average value: 1.23 g/cc Grade Count:119 |
| Filler Content | 5.00 - 15.0 % | 5.00 - 15.0 % | Average value: 11.3 % Grade Count:31 |
| Water Absorption | 0.0900 - 8.30 % | 0.0900 - 8.30 % | Average value: 2.46 % Grade Count:58 |
| Moisture Absorption at Equilibrium | 1.20 - 3.00 % | 1.20 - 3.00 % | Average value: 2.13 % Grade Count:21 |
| Water Absorption at Saturation | 7.00 - 9.50 % | 7.00 - 9.50 % | Average value: 8.31 % Grade Count:8 |
| Viscosity | 2.60 - 50.0 cP | 2.60 - 50.0 cP | Average value: 18.4 cP Grade Count:3 |
| Viscosity Measurement | 0.630 - 145 | 0.630 - 145 | Average value: 56.5 Grade Count:19 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00646 cm/cm Grade Count:100 |
| 0.00500 - 0.00500 cm/cm @Temperature 80.0 - 80.0 °C | 0.00500 - 0.00500 in/in @Temperature 176 - 176 °F | Average value: 0.00500 cm/cm Grade Count:1 | |
| Linear Mold Shrinkage, 6.35 mm section | 0.00800 - 0.0100 cm/cm | 0.00800 - 0.0100 in/in | Average value: 0.00900 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00680 - 0.0197 cm/cm | 0.00680 - 0.0197 in/in | Average value: 0.0128 cm/cm Grade Count:20 |
| 0.00900 - 0.00900 cm/cm @Temperature 80.0 - 80.0 °C | 0.00900 - 0.00900 in/in @Temperature 176 - 176 °F | Average value: 0.00900 cm/cm Grade Count:1 | |
| Melt Flow | 2.00 - 93.8 g/10 min | 2.00 - 93.8 g/10 min | Average value: 17.8 g/10 min Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 - 122 | 100 - 122 | Average value: 119 Grade Count:37 |
| Hardness, Shore D | 73.0 - 81.0 | 73.0 - 81.0 | Average value: 77.3 Grade Count:4 |
| Ball Indentation Hardness | 95.0 - 155 MPa | 13800 - 22500 psi | Average value: 127 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 40.0 - 165 MPa | 5800 - 23900 psi | Average value: 97.5 MPa Grade Count:81 |
| 20.0 - 170 MPa @Temperature -40.0 - 121 °C | 2900 - 24700 psi @Temperature -40.0 - 250 °F | Average value: 70.7 MPa Grade Count:7 | |
| 27.5 - 52.5 MPa @Temperature 130 - 175 °C | 3990 - 7610 psi @Temperature 266 - 347 °F | Average value: 70.7 MPa Grade Count:2 | |
| 27.5 - 52.5 MPa @Time 1.80e+7 - 7.20e+7 sec | 3990 - 7610 psi @Time 5000 - 20000 hour | Average value: 70.7 MPa Grade Count:2 | |
| Tensile Strength, Yield | 51.7 - 162 MPa | 7500 - 23500 psi | Average value: 97.8 MPa Grade Count:44 |
| Elongation at Break | 2.00 - 30.0 % | 2.00 - 30.0 % | Average value: 5.61 % Grade Count:93 |
| 2.00 - 30.0 % @Temperature -40.0 - 121 °C | 2.00 - 30.0 % @Temperature -40.0 - 250 °F | Average value: 9.69 % Grade Count:7 | |
| Elongation at Yield | 1.60 - 15.0 % | 1.60 - 15.0 % | Average value: 4.93 % Grade Count:21 |
| Modulus of Elasticity | 2.64 - 16.0 GPa | 383 - 2320 ksi | Average value: 5.03 GPa Grade Count:49 |
| 1.445 - 6.90 GPa @Temperature -40.0 - 120 °C | 209.6 - 1000 ksi @Temperature -40.0 - 248 °F | Average value: 3.52 GPa Grade Count:6 | |
| Flexural Yield Strength | 13.8 - 250 MPa | 2000 - 36300 psi | Average value: 139 MPa Grade Count:110 |
| 49.987 - 265 MPa @Temperature -40.0 - 121 °C | 7250.0 - 38400 psi @Temperature -40.0 - 250 °F | Average value: 147 MPa Grade Count:5 | |
| Flexural Modulus | 0.0343 - 24.0 GPa | 4.98 - 3480 ksi | Average value: 4.38 GPa Grade Count:112 |
| 0.992845 - 5.19865 GPa @Temperature -40.0 - 121 °C | 144.002 - 754.012 ksi @Temperature -40.0 - 250 °F | Average value: 2.30 GPa Grade Count:3 | |
| Compressive Yield Strength | 100 - 117 MPa | 14500 - 17000 psi | Average value: 111 MPa Grade Count:3 |
| Izod Impact, Notched | 0.290 - 1.95 J/cm | 0.543 - 3.65 ft-lb/in | Average value: 0.718 J/cm Grade Count:78 |
| 0.37373 - 0.400 J/cm @Temperature -40.0 - -40.0 °C | 0.70015 - 0.749 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.391 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 4.27 - 5.34 J/cm | 8.00 - 10.0 ft-lb/in | Average value: 4.94 J/cm Grade Count:12 |
| Izod Impact, Notched (ISO) | 3.80 - 10.0 kJ/m² | 1.81 - 4.76 ft-lb/in² | Average value: 5.97 kJ/m² Grade Count:11 |
| 5.00 - 8.00 kJ/m² @Temperature -30.0 - -30.0 °C | 2.38 - 3.81 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 6.50 kJ/m² Grade Count:2 | |
| Izod Impact, Unnotched (ISO) | 38.0 - 38.0 kJ/m² @Temperature -30.0 - -30.0 °C | 18.1 - 18.1 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 38.0 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 2.00 J/cm² - NB | 9.52 ft-lb/in² - NB | Average value: 4.77 J/cm² Grade Count:27 |
| 1.50 J/cm² - NB @Temperature -40.0 - -20.0 °C | 7.14 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 3.71 J/cm² Grade Count:16 | |
| Charpy Impact, Notched | 0.100 - 2.10 J/cm² | 0.476 - 9.99 ft-lb/in² | Average value: 0.901 J/cm² Grade Count:35 |
| 0.100 - 20.0 J/cm² @Temperature -40.0 - -20.0 °C | 0.476 - 95.2 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 2.21 J/cm² Grade Count:22 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+17 ohm-cm | 1.00 - 1.00e+17 ohm-cm | Average value: 2.63e+15 ohm-cm Grade Count:46 |
| Surface Resistance | 10.0 - 3.10e+15 ohm | 10.0 - 3.10e+15 ohm | Average value: 3.01e+14 ohm Grade Count:17 |
| Insulation Resistance | 10000 - 1.00e+11 ohm | 10000 - 1.00e+11 ohm | Average value: 3.33e+10 ohm Grade Count:3 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:4 |
| Shielding Effectiveness | 50.0 dB | 50.0 dB | Average value: 50.0 dB Grade Count:3 |
| Dielectric Constant | 2.60 - 7.00 | 2.60 - 7.00 | Average value: 3.90 Grade Count:12 |
| Dielectric Strength | 11.0 - 80.0 kV/mm | 280 - 2030 kV/in | Average value: 23.9 kV/mm Grade Count:27 |
| Dissipation Factor | 0.0100 - 0.0700 | 0.0100 - 0.0700 | Average value: 0.0292 Grade Count:11 |
| Arc Resistance | 112 - 160 sec | 112 - 160 sec | Average value: 131 sec Grade Count:5 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 483 V Grade Count:15 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.350 - 97.0 µm/m-°C | 0.194 - 53.9 µin/in-°F | Average value: 45.4 µm/m-°C Grade Count:32 |
| CTE, linear, Transverse to Flow | 12.0 - 78.0 µm/m-°C | 6.67 - 43.3 µin/in-°F | Average value: 60.0 µm/m-°C Grade Count:4 |
| Specific Heat Capacity | 1.40 - 2.73 J/g-°C | 0.335 - 0.652 BTU/lb-°F | Average value: 2.06 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.230 - 3.50 W/m-K | 1.60 - 24.3 BTU-in/hr-ft²-°F | Average value: 0.836 W/m-K Grade Count:6 |
| Melting Point | 215 - 260 °C | 419 - 500 °F | Average value: 220 °C Grade Count:60 |
| Maximum Service Temperature, Air | 90.0 - 210 °C | 194 - 410 °F | Average value: 133 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 - 222 °C | 370 - 432 °F | Average value: 209 °C Grade Count:60 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 232 °C | 131 - 450 °F | Average value: 187 °C Grade Count:100 |
| Vicat Softening Point | 195 - 250 °C | 383 - 482 °F | Average value: 204 °C Grade Count:17 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:64 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 721 °C Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 275 °C | 176 - 527 °F | Average value: 239 °C Grade Count:21 |
| Feed Temperature | 60.0 - 280 °C | 140 - 536 °F | Average value: 135 °C Grade Count:3 |
| Nozzle Temperature | 238 - 293 °C | 460 - 560 °F | Average value: 264 °C Grade Count:15 |
| Melt Temperature | 80.0 - 304 °C | 176 - 580 °F | Average value: 259 °C Grade Count:52 |
| Mold Temperature | 21.1 - 121 °C | 70.0 - 250 °F | Average value: 82.1 °C Grade Count:62 |
| Drying Temperature | 75.0 - 130 °C | 167 - 266 °F | Average value: 83.7 °C Grade Count:38 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.87 hour Grade Count:27 |
| 2.00 - 4.00 hour @Temperature 79.4 - 104 °C | 2.00 - 4.00 hour @Temperature 175 - 220 °F | Average value: 3.00 hour Grade Count:7 | |
| Moisture Content | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.160 % Grade Count:21 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 4.96 - 172 MPa | 720 - 25000 psi | Average value: 61.0 MPa Grade Count:35 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.420 MPa Grade Count:15 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 53.9 % Grade Count:9 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 64.5 rpm Grade Count:15 |