- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.25
- 拉伸强度 [MPa]: 30.0
- 断裂伸长率 [%]: 50.0
- 弯曲强度 [MPa]: 17.2
- 弯曲模量 [MPa]: 0.0588
- 硬度: 100.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 1.62 g/cc | 0.0434 - 0.0585 lb/in³ | Average value: 1.38 g/cc Grade Count:76 |
| Filler Content | 25.0 - 30.0 % | 25.0 - 30.0 % | Average value: 28.3 % Grade Count:3 |
| Water Absorption | 0.200 - 8.00 % | 0.200 - 8.00 % | Average value: 3.82 % Grade Count:51 |
| Moisture Absorption at Equilibrium | 0.170 - 3.00 % | 0.170 - 3.00 % | Average value: 1.86 % Grade Count:33 |
| Water Absorption at Saturation | 6.00 - 7.50 % | 6.00 - 7.50 % | Average value: 6.56 % Grade Count:5 |
| Viscosity Measurement | 0.840 - 145 | 0.840 - 145 | Average value: 132 Grade Count:11 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:4 |
| Linear Mold Shrinkage | 0.00150 - 0.0190 cm/cm | 0.00150 - 0.0190 in/in | Average value: 0.00816 cm/cm Grade Count:60 |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.0189 cm/cm | 0.00400 - 0.0189 in/in | Average value: 0.00901 cm/cm Grade Count:26 |
| Melt Flow | 3.00 - 81.6 g/10 min | 3.00 - 81.6 g/10 min | Average value: 43.7 g/10 min Grade Count:21 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 82.0 - 93.0 | 82.0 - 93.0 | Average value: 86.4 Grade Count:7 |
| Hardness, Rockwell R | 100 - 121 | 100 - 121 | Average value: 117 Grade Count:7 |
| Hardness, Shore D | 73.0 - 85.0 | 73.0 - 85.0 | Average value: 80.5 Grade Count:4 |
| Ball Indentation Hardness | 70.0 - 205 MPa | 10200 - 29700 psi | Average value: 151 MPa Grade Count:10 |
| Tensile Strength, Ultimate | 17.2 - 128 MPa | 2500 - 18500 psi | Average value: 64.4 MPa Grade Count:53 |
| 23.0 - 107 MPa @Temperature -40.0 - 120 °C | 3340 - 15500 psi @Temperature -40.0 - 248 °F | Average value: 40.4 MPa Grade Count:5 | |
| 5.15 - 113.65 MPa @Temperature -20.0 - 150 °C | 747 - 16484 psi @Temperature -4.00 - 302 °F | Average value: 40.4 MPa Grade Count:1 | |
| 5.15 - 113.65 MPa @Strain 0.390 - 15.6 % | 747 - 16484 psi @Strain 0.390 - 15.6 % | Average value: 40.4 MPa Grade Count:1 | |
| Tensile Strength, Yield | 30.0 - 103 MPa | 4350 - 14900 psi | Average value: 72.3 MPa Grade Count:23 |
| Elongation at Break | 1.00 - 70.0 % | 1.00 - 70.0 % | Average value: 14.9 % Grade Count:59 |
| Elongation at Yield | 2.50 - 40.0 % | 2.50 - 40.0 % | Average value: 9.84 % Grade Count:9 |
| Modulus of Elasticity | 1.70 - 9.00 GPa | 247 - 1310 ksi | Average value: 4.63 GPa Grade Count:45 |
| Flexural Yield Strength | 50.0 - 190 MPa | 7250 - 27500 psi | Average value: 115 MPa Grade Count:40 |
| 53.0 - 168 MPa @Temperature -40.0 - 80.0 °C | 7690 - 24400 psi @Temperature -40.0 - 176 °F | Average value: 114 MPa Grade Count:1 | |
| Flexural Modulus | 0.0588 - 7.58 GPa | 8.53 - 1100 ksi | Average value: 4.13 GPa Grade Count:47 |
| 0.800 - 8.00 GPa @Temperature -40.0 - 120 °C | 116 - 1160 ksi @Temperature -40.0 - 248 °F | Average value: 2.45 GPa Grade Count:5 | |
| Izod Impact, Notched | 0.250 - 2.60 J/cm | 0.468 - 4.87 ft-lb/in | Average value: 0.662 J/cm Grade Count:25 |
| 0.200 - 0.680 J/cm @Temperature -40.0 - -20.0 °C | 0.375 - 1.27 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.370 J/cm Grade Count:4 | |
| Izod Impact, Notched (ISO) | 2.60 - 15.0 kJ/m² | 1.24 - 7.14 ft-lb/in² | Average value: 8.03 kJ/m² Grade Count:16 |
| 4.00 - 8.00 kJ/m² @Temperature -30.0 - -30.0 °C | 1.90 - 3.81 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.67 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 35.0 - 35.0 kJ/m² @Temperature -30.0 - -30.0 °C | 16.7 - 16.7 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 35.0 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 1.30 J/cm² - NB | 6.19 ft-lb/in² - NB | Average value: 8.37 J/cm² Grade Count:47 |
| 1.20 J/cm² - NB @Temperature -40.0 - 30.0 °C | 5.71 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 5.29 J/cm² Grade Count:27 | |
| Charpy Impact, Notched | 0.280 - 1.80 J/cm² | 1.33 - 8.57 ft-lb/in² | Average value: 0.732 J/cm² Grade Count:39 |
| 0.100 - 1.00 J/cm² @Temperature -30.0 - 30.0 °C | 0.476 - 4.76 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.438 J/cm² Grade Count:21 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 17.5 MPa @Temperature 60.0 - 90.0 °C | 0.000 - 2540 psi @Temperature 140 - 194 °F | Average value: 6.88 MPa Grade Count:1 |
| 0.000 - 17.5 MPa @Strain 0.000 - 3.04 % | 0.000 - 2540 psi @Strain 0.000 - 3.04 % | Average value: 6.88 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 800 MPa | 0.000 - 116000 psi | Average value: 95.6 MPa Grade Count:4 |
| 0.000 - 17.5 MPa @Temperature 60.0 - 90.0 °C | 0.000 - 2540 psi @Temperature 140 - 194 °F | Average value: 6.88 MPa Grade Count:1 | |
| 0.000 - 17.5 MPa @Strain 0.000 - 3.78 % | 0.000 - 2540 psi @Strain 0.000 - 3.78 % | Average value: 6.88 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+16 ohm-cm | 1.00e+9 - 1.00e+16 ohm-cm | Average value: 7.30e+14 ohm-cm Grade Count:39 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 1.47e+15 ohm Grade Count:22 |
| Dielectric Constant | 3.00 - 15.0 | 3.00 - 15.0 | Average value: 5.03 Grade Count:18 |
| Dielectric Strength | 11.8 - 100 kV/mm | 300 - 2540 kV/in | Average value: 28.7 kV/mm Grade Count:26 |
| Dissipation Factor | 0.00500 - 0.350 | 0.00500 - 0.350 | Average value: 0.0868 Grade Count:17 |
| Arc Resistance | 120 - 185 sec | 120 - 185 sec | Average value: 155 sec Grade Count:3 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 482 V Grade Count:42 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.500 - 500 µm/m-°C | 0.278 - 278 µin/in-°F | Average value: 81.4 µm/m-°C Grade Count:28 |
| CTE, linear, Transverse to Flow | 0.500 - 102 µm/m-°C | 0.278 - 56.7 µin/in-°F | Average value: 53.7 µm/m-°C Grade Count:14 |
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | Average value: 0.310 W/m-K Grade Count:6 |
| Melting Point | 210 - 225 °C | 410 - 437 °F | Average value: 220 °C Grade Count:57 |
| Maximum Service Temperature, Air | 65.0 - 180 °C | 149 - 356 °F | Average value: 130 °C Grade Count:16 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 - 240 °C | 374 - 464 °F | Average value: 201 °C Grade Count:33 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 250 °C | 149 - 482 °F | Average value: 121 °C Grade Count:61 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:3 |
| Vicat Softening Point | 191 - 255 °C | 376 - 491 °F | Average value: 206 °C Grade Count:20 |
| Decomposition Temperature | 300 °C | 572 °F | Average value: 300 °C Grade Count:4 |
| UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 108 °C Grade Count:11 |
| UL RTI, Mechanical with Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 90.7 °C Grade Count:11 |
| UL RTI, Mechanical without Impact | 65.0 - 140 °C | 149 - 284 °F | Average value: 108 °C Grade Count:11 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:55 |
| Oxygen Index | 22.0 - 32.0 % | 22.0 - 32.0 % | Average value: 25.4 % Grade Count:11 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 753 °C Grade Count:22 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 163 °C Grade Count:7 |
| Feed Temperature | 60.0 - 235 °C | 140 - 455 °F | Average value: 111 °C Grade Count:4 |
| Nozzle Temperature | 210 - 293 °C | 410 - 560 °F | Average value: 257 °C Grade Count:5 |
| Melt Temperature | 80.0 - 370 °C | 176 - 698 °F | Average value: 258 °C Grade Count:43 |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | Average value: 80.8 °C Grade Count:34 |
| Drying Temperature | 75.0 - 110 °C | 167 - 230 °F | Average value: 85.1 °C Grade Count:34 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.60 hour Grade Count:24 |
| Moisture Content | 0.0500 - 2.00 % | 0.0500 - 2.00 % | Average value: 0.275 % Grade Count:14 |
| Injection Pressure | 30.0 - 138 MPa | 4350 - 20000 psi | Average value: 90.6 MPa Grade Count:10 |