- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.938
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.085
- 拉伸强度 [MPa]: 25.0
- 断裂伸长率 [%]: 7.00
- 弯曲强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 0.0143
- 硬度: 40.0
- 热变形温度 [℃]: 53.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 - 2.50 g/cc | 0.0339 - 0.0903 lb/in³ | Average value: 1.15 g/cc Grade Count:244 |
| Water Absorption | 0.0600 - 9.50 % | 0.0600 - 9.50 % | Average value: 2.46 % Grade Count:148 |
| Moisture Absorption at Equilibrium | 0.170 - 3.40 % | 0.170 - 3.40 % | Average value: 2.27 % Grade Count:78 |
| Water Absorption at Saturation | 6.70 - 10.0 % | 6.70 - 10.0 % | Average value: 8.33 % Grade Count:25 |
| Viscosity Measurement | 0.580 - 2.56 | 0.580 - 2.56 | Average value: 1.89 Grade Count:7 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:6 |
| Linear Mold Shrinkage | 0.000100 - 0.0350 cm/cm | 0.000100 - 0.0350 in/in | Average value: 0.0124 cm/cm Grade Count:192 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0253 cm/cm | 0.00200 - 0.0253 in/in | Average value: 0.0153 cm/cm Grade Count:44 |
| Melt Flow | 3.00 - 121 g/10 min | 3.00 - 121 g/10 min | Average value: 33.2 g/10 min Grade Count:24 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 50.0 - 85.0 | 50.0 - 85.0 | Average value: 72.5 Grade Count:6 |
| Hardness, Rockwell R | 40.0 - 125 | 40.0 - 125 | Average value: 106 Grade Count:94 |
| Hardness, Shore D | 52.0 - 82.0 | 52.0 - 82.0 | Average value: 71.6 Grade Count:16 |
| Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | Average value: 113 MPa Grade Count:8 |
| Tensile Strength, Ultimate | 22.0 - 200 MPa | 3190 - 29000 psi | Average value: 60.8 MPa Grade Count:94 |
| 70.0 - 100 MPa @Temperature -40.0 - -40.0 °C | 10200 - 14500 psi @Temperature -40.0 - -40.0 °F | Average value: 85.0 MPa Grade Count:4 | |
| Tensile Strength, Yield | 25.0 - 207 MPa | 3630 - 30000 psi | Average value: 67.6 MPa Grade Count:157 |
| 12.0 - 117 MPa @Temperature -40.0 - 120 °C | 1740 - 17000 psi @Temperature -40.0 - 248 °F | Average value: 56.9 MPa Grade Count:8 | |
| Elongation at Break | 1.50 - 500 % | 1.50 - 500 % | Average value: 80.1 % Grade Count:213 |
| 9.00 - 20.0 % @Temperature -40.0 - -40.0 °C | 9.00 - 20.0 % @Temperature -40.0 - -40.0 °F | Average value: 14.5 % Grade Count:4 | |
| Elongation at Yield | 3.50 - 350 % | 3.50 - 350 % | Average value: 24.1 % Grade Count:64 |
| 4.00 - 37.0 % @Temperature -40.0 - 120 °C | 4.00 - 37.0 % @Temperature -40.0 - 248 °F | Average value: 23.7 % Grade Count:6 | |
| Modulus of Elasticity | 0.210 - 14.5 GPa | 30.5 - 2100 ksi | Average value: 2.30 GPa Grade Count:93 |
| 0.145 - 3.30 GPa @Temperature -40.0 - 120 °C | 21.0 - 479 ksi @Temperature -40.0 - 248 °F | Average value: 1.13 GPa Grade Count:7 | |
| Flexural Yield Strength | 7.00 - 310 MPa | 1020 - 45000 psi | Average value: 87.0 MPa Grade Count:186 |
| 8.00 - 148 MPa @Temperature -40.0 - 120 °C | 1160 - 21500 psi @Temperature -40.0 - 248 °F | Average value: 55.1 MPa Grade Count:8 | |
| Flexural Modulus | 0.0143 - 12.8 GPa | 2.08 - 1860 ksi | Average value: 2.50 GPa Grade Count:207 |
| 0.145 - 0.415 GPa @Temperature 65.0 - 120 °C | 21.0 - 60.2 ksi @Temperature 149 - 248 °F | Average value: 0.262 GPa Grade Count:5 | |
| Compressive Yield Strength | 24.0 - 120 MPa | 3480 - 17400 psi | Average value: 61.6 MPa Grade Count:7 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:6 |
| Izod Impact, Notched | 0.0850 J/cm - NB | 0.159 ft-lb/in - NB | Average value: 33.7 J/cm Grade Count:155 |
| 0.350 - 7.00 J/cm @Temperature -40.0 - -20.0 °C | 0.656 - 13.1 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.62 J/cm Grade Count:13 | |
| 0.588399 - 5338.47 J/cm @Temperature -40.0 - -20.0 °C | 1.10231 - 10001.1 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.62 J/cm Grade Count:22 | |
| 0.588399 - 5338.47 J/cm @Thickness 3.17 - 6.40 mm | 1.10231 - 10001.1 ft-lb/in @Thickness 0.125 - 0.252 in | Average value: 1.62 J/cm Grade Count:22 | |
| Izod Impact, Unnotched | 13.9 J/cm - NB | 26.0 ft-lb/in - NB | Average value: 14.6 J/cm Grade Count:35 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² - NB | 4.76 ft-lb/in² - NB | Average value: 43.4 kJ/m² Grade Count:40 |
| 5.00 - 85.0 kJ/m² @Temperature -40.0 - -30.0 °C | 2.38 - 40.4 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 22.3 kJ/m² Grade Count:24 | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² - NB | 35.7 ft-lb/in² - NB | Average value: 90.3 kJ/m² Grade Count:18 |
| 65.0 kJ/m² - NB @Temperature -30.0 - -30.0 °C | 30.9 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 77.5 kJ/m² Grade Count:14 | |
| Charpy Impact Unnotched | 7.20 J/cm² - NB | 34.3 ft-lb/in² - NB | Average value: 12.5 J/cm² Grade Count:69 |
| 7.00 J/cm² - NB @Temperature -70.0 - -20.0 °C | 33.3 ft-lb/in² - NB @Temperature -94.0 - -4.00 °F | Average value: 15.8 J/cm² Grade Count:40 | |
| Charpy Impact, Notched | 0.400 J/cm² - NB | 1.90 ft-lb/in² - NB | Average value: 4.08 J/cm² Grade Count:76 |
| 0.300 - 8.50 J/cm² @Temperature -40.0 - -20.0 °C | 1.43 - 40.5 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 1.89 J/cm² Grade Count:47 | |
| Puncture Energy | 50.0 - 65.0 J | 36.9 - 47.9 ft-lb | Average value: 60.8 J Grade Count:4 |
| 64.0 - 64.0 J @Temperature -30.0 - -30.0 °C | 47.2 - 47.2 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 60.9 J Grade Count:1 | |
| 50.0 - 67.0 J @Temperature -30.0 - -30.0 °C | 36.9 - 49.4 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 60.9 J Grade Count:3 | |
| 50.0 - 67.0 J @Load <=5810 kg | 36.9 - 49.4 ft-lb @Load <=12800 lb | Average value: 60.9 J Grade Count:3 | |
| Taber Abrasion, mg/1000 Cycles | 8.00 - 19.0 | 8.00 - 19.0 | Average value: 13.5 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+17 ohm-cm | 100 - 1.00e+17 ohm-cm | Average value: 1.54e+15 ohm-cm Grade Count:115 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 1.01e+14 ohm Grade Count:52 |
| Dielectric Constant | 2.70 - 15.4 | 2.70 - 15.4 | Average value: 5.49 Grade Count:48 |
| Dielectric Strength | 11.8 - 100 kV/mm | 300 - 2540 kV/in | Average value: 26.7 kV/mm Grade Count:102 |
| Dissipation Factor | 0.00300 - 0.400 | 0.00300 - 0.400 | Average value: 0.137 Grade Count:15 |
| Dielectric Loss Index | 0.0190 - 0.300 | 0.0190 - 0.300 | Average value: 0.132 Grade Count:13 |
| Arc Resistance | 113 - 195 sec | 113 - 195 sec | Average value: 159 sec Grade Count:12 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Average value: 579 V Grade Count:51 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.700 - 200 µm/m-°C | 0.389 - 111 µin/in-°F | Average value: 73.9 µm/m-°C Grade Count:102 |
| CTE, linear, Transverse to Flow | 93.0 - 200 µm/m-°C | 51.7 - 111 µin/in-°F | Average value: 133 µm/m-°C Grade Count:17 |
| Specific Heat Capacity | 1.50 - 3.89 J/g-°C | 0.359 - 0.930 BTU/lb-°F | Average value: 2.50 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.168 - 0.320 W/m-K | 1.17 - 2.22 BTU-in/hr-ft²-°F | Average value: 0.248 W/m-K Grade Count:6 |
| Melting Point | 205 - 260 °C | 401 - 500 °F | Average value: 219 °C Grade Count:136 |
| Maximum Service Temperature, Air | 70.0 - 200 °C | 158 - 392 °F | Average value: 119 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 - 250 °C | 127 - 482 °F | Average value: 161 °C Grade Count:124 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 - 230 °C | 100 - 446 °F | Average value: 82.4 °C Grade Count:199 |
| Vicat Softening Point | 100 - 225 °C | 212 - 437 °F | Average value: 183 °C Grade Count:39 |
| UL RTI, Electrical | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.7 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.7 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 60.0 - 65.0 °C | 140 - 149 °F | Average value: 61.7 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:126 |
| Glow Wire Test | 650 - 850 °C | 1200 - 1560 °F | Average value: 733 °C Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 300 °C | 430 - 572 °F | Average value: 260 °C Grade Count:27 |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Average value: 70.0 °C Grade Count:10 |
| Nozzle Temperature | 240 - 290 °C | 464 - 554 °F | Average value: 261 °C Grade Count:18 |
| Melt Temperature | 80.0 - 290 °C | 176 - 554 °F | Average value: 250 °C Grade Count:96 |
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | Average value: 71.0 °C Grade Count:99 |
| Drying Temperature | 70.0 - 110 °C | 158 - 230 °F | Average value: 81.4 °C Grade Count:80 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.64 hour Grade Count:59 |
| 2.00 - 6.00 hour @Temperature 79.4 - 121 °C | 2.00 - 6.00 hour @Temperature 175 - 250 °F | Average value: 3.14 hour Grade Count:7 | |
| Moisture Content | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.158 % Grade Count:46 |
| Injection Pressure | 4.14 - 150 MPa | 600 - 21800 psi | Average value: 66.1 MPa Grade Count:29 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:10 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 2.98 MPa Grade Count:18 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:7 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 69.2 rpm Grade Count:18 |