- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.64
- 拉伸强度 [MPa]: 6.0
- 断裂伸长率 [%]: 55.0
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 110.0
- 热变形温度 [℃]: 193.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.53 g/cc | 0.0415 - 0.0553 lb/in³ | Average value: 1.29 g/cc Grade Count:91 |
| Filler Content | 5.00 - 50.0 % | 5.00 - 50.0 % | Average value: 27.0 % Grade Count:10 |
| Water Absorption | 0.600 - 7.00 % | 0.600 - 7.00 % | Average value: 1.98 % Grade Count:45 |
| Moisture Absorption at Equilibrium | 1.40 - 2.50 % | 1.40 - 2.50 % | Average value: 1.90 % Grade Count:33 |
| Water Absorption at Saturation | 4.80 - 8.50 % | 4.80 - 8.50 % | Average value: 6.33 % Grade Count:15 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | Average value: 150 cm³/g Grade Count:3 |
| Linear Mold Shrinkage | 0.000600 - 0.0110 cm/cm | 0.000600 - 0.0110 in/in | Average value: 0.00367 cm/cm Grade Count:75 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0120 cm/cm | 0.00300 - 0.0120 in/in | Average value: 0.00600 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0140 cm/cm | 0.00100 - 0.0140 in/in | Average value: 0.00752 cm/cm Grade Count:33 |
| Melt Flow | 1.00 - 45.0 g/10 min | 1.00 - 45.0 g/10 min | Average value: 25.3 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76.0 - 121 | 76.0 - 121 | Average value: 83.9 Grade Count:13 |
| Hardness, Rockwell R | 110 - 120 | 110 - 120 | Average value: 117 Grade Count:23 |
| Ball Indentation Hardness | 55.0 - 195 MPa | 7980 - 28300 psi | Average value: 126 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 40.0 - 190 MPa | 5800 - 27600 psi | Average value: 113 MPa Grade Count:86 |
| Tensile Strength, Yield | 6.00 - 170 MPa | 870 - 24700 psi | Average value: 102 MPa Grade Count:11 |
| Elongation at Break | 2.20 - 28.0 % | 2.20 - 28.0 % | Average value: 5.40 % Grade Count:88 |
| Elongation at Yield | 2.90 - 5.50 % | 2.90 - 5.50 % | Average value: 4.40 % Grade Count:6 |
| Modulus of Elasticity | 0.930 - 13.8 GPa | 135 - 2000 ksi | Average value: 6.51 GPa Grade Count:67 |
| Flexural Yield Strength | 55.0 - 290 MPa | 7980 - 42100 psi | Average value: 171 MPa Grade Count:71 |
| Flexural Modulus | 2.10 - 11.7 GPa | 305 - 1700 ksi | Average value: 6.06 GPa Grade Count:74 |
| Compressive Yield Strength | 62.1 - 172 MPa | 9000 - 24900 psi | Average value: 119 MPa Grade Count:14 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:11 |
| Shear Modulus | 1.60 - 4.40 GPa | 232 - 638 ksi | Average value: 3.15 GPa Grade Count:8 |
| Izod Impact, Notched | 0.640 - 2.14 J/cm | 1.20 - 4.00 ft-lb/in | Average value: 1.54 J/cm Grade Count:30 |
| Izod Impact, Unnotched | 5.82 J/cm - NB | 10.9 ft-lb/in - NB | Average value: 10.1 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 10.0 - 35.0 kJ/m² | 4.76 - 16.7 ft-lb/in² | Average value: 18.4 kJ/m² Grade Count:16 |
| 7.00 - 18.0 kJ/m² @Temperature -30.0 - -30.0 °C | 3.33 - 8.57 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 11.2 kJ/m² Grade Count:12 | |
| Izod Impact, Unnotched (ISO) | 55.0 - 95.0 kJ/m² | 26.2 - 45.2 ft-lb/in² | Average value: 74.3 kJ/m² Grade Count:14 |
| 35.0 - 90.0 kJ/m² @Temperature -30.0 - -30.0 °C | 16.7 - 42.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 64.9 kJ/m² Grade Count:13 | |
| Charpy Impact Unnotched | 5.00 J/cm² - NB | 23.8 ft-lb/in² - NB | Average value: 8.74 J/cm² Grade Count:40 |
| 4.50 - 11.5 J/cm² @Temperature -40.0 - -20.0 °C | 21.4 - 54.7 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 7.61 J/cm² Grade Count:26 | |
| Charpy Impact, Notched | 0.700 - 4.20 J/cm² | 3.33 - 20.0 ft-lb/in² | Average value: 2.14 J/cm² Grade Count:46 |
| 0.610 - 2.00 J/cm² @Temperature -30.0 - -20.0 °C | 2.90 - 9.52 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 1.17 J/cm² Grade Count:29 | |
| Puncture Energy | 3.80 - 32.0 J | 2.80 - 23.6 ft-lb | Average value: 11.4 J Grade Count:4 |
| 2.50 - 4.80 J @Temperature -30.0 - -30.0 °C | 1.84 - 3.54 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 3.10 J Grade Count:4 | |
| 2.50 - 4.80 J @Load <=78.5 kg | 1.84 - 3.54 ft-lb @Load <=173 lb | Average value: 3.10 J Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+15 ohm-cm | 1.00e+12 - 1.00e+15 ohm-cm | Average value: 4.45e+14 ohm-cm Grade Count:35 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 1.56e+15 ohm Grade Count:19 |
| Dielectric Constant | 3.20 - 14.0 | 3.20 - 14.0 | Average value: 5.65 Grade Count:21 |
| Dielectric Strength | 19.7 - 43.0 kV/mm | 500 - 1090 kV/in | Average value: 31.2 kV/mm Grade Count:24 |
| Dissipation Factor | 0.00600 - 0.300 | 0.00600 - 0.300 | Average value: 0.0817 Grade Count:9 |
| Dielectric Loss Index | 0.0200 - 0.220 | 0.0200 - 0.220 | Average value: 0.113 Grade Count:12 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Average value: 150 sec Grade Count:4 |
| Comparative Tracking Index | 450 - 600 V | 450 - 600 V | Average value: 562 V Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.0 - 50.0 µm/m-°C | 10.6 - 27.8 µin/in-°F | Average value: 29.5 µm/m-°C Grade Count:25 |
| CTE, linear, Transverse to Flow | 65.0 - 150 µm/m-°C | 36.1 - 83.3 µin/in-°F | Average value: 98.7 µm/m-°C Grade Count:13 |
| Thermal Conductivity | 0.200 - 0.389 W/m-K | 1.39 - 2.70 BTU-in/hr-ft²-°F | Average value: 0.312 W/m-K Grade Count:3 |
| Melting Point | 205 - 225 °C | 401 - 437 °F | Average value: 218 °C Grade Count:73 |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 - 220 °C | 380 - 428 °F | Average value: 211 °C Grade Count:58 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 213 °C | 158 - 415 °F | Average value: 194 °C Grade Count:72 |
| Vicat Softening Point | 185 - 215 °C | 365 - 419 °F | Average value: 201 °C Grade Count:21 |
| Flammability, UL94 | HB | HB | Grade Count:49 |
| Glow Wire Test | 550 - 650 °C | 1020 - 1200 °F | Average value: 607 °C Grade Count:7 |
| Shrinkage | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.104 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 290 °C | 430 - 554 °F | Average value: 264 °C Grade Count:26 |
| Melt Temperature | 220 - 291 °C | 428 - 556 °F | Average value: 269 °C Grade Count:36 |
| Mold Temperature | 54.4 - 121 °C | 130 - 250 °F | Average value: 82.9 °C Grade Count:57 |
| Drying Temperature | 75.0 - 100 °C | 167 - 212 °F | Average value: 83.9 °C Grade Count:33 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.94 hour Grade Count:8 |
| 2.00 - 6.00 hour @Temperature 80.0 - 80.0 °C | 2.00 - 6.00 hour @Temperature 176 - 176 °F | Average value: 4.00 hour Grade Count:8 | |
| Moisture Content | 0.0300 - 1.80 % | 0.0300 - 1.80 % | Average value: 0.173 % Grade Count:23 |
| Injection Pressure | 68.9 - 130 MPa | 10000 - 18900 psi | Average value: 91.2 MPa Grade Count:13 |