- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.92
- 吸水率 [%]: 0.8
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 35.0
- 断裂伸长率 [%]: 10.3
- 弯曲强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 110.0
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 - 1.66 g/cc | 0.0332 - 0.0600 lb/in³ | Average value: 1.36 g/cc Grade Count:91 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 26.7 % Grade Count:6 |
| Water Absorption | 0.800 - 8.00 % | 0.800 - 8.00 % | Average value: 2.58 % Grade Count:36 |
| Moisture Absorption at Equilibrium | 0.250 - 3.00 % | 0.250 - 3.00 % | Average value: 1.94 % Grade Count:33 |
| Water Absorption at Saturation | 5.80 - 7.00 % | 5.80 - 7.00 % | Average value: 6.40 % Grade Count:4 |
| Viscosity Measurement | 1.03 - 140 | 1.03 - 140 | Average value: 36.2 Grade Count:8 |
| Viscosity Test | 140 - 150 cm³/g | 140 - 150 cm³/g | Average value: 145 cm³/g Grade Count:4 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00907 cm/cm Grade Count:80 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00800 - 0.0170 cm/cm | 0.00800 - 0.0170 in/in | Average value: 0.0135 cm/cm Grade Count:6 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0197 cm/cm | 0.00200 - 0.0197 in/in | Average value: 0.0123 cm/cm Grade Count:23 |
| Melt Flow | 3.00 - 115 g/10 min | 3.00 - 115 g/10 min | Average value: 37.2 g/10 min Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 122 | 110 - 122 | Average value: 118 Grade Count:13 |
| Hardness, Shore D | 80.0 - 90.0 | 80.0 - 90.0 | Average value: 85.4 Grade Count:4 |
| Ball Indentation Hardness | 75.0 - 220 MPa | 10900 - 31900 psi | Average value: 154 MPa Grade Count:6 |
| Tensile Strength, Ultimate | 30.0 - 147 MPa | 4350 - 21300 psi | Average value: 71.6 MPa Grade Count:74 |
| 23.0 - 39.0 MPa @Temperature 60.0 - 120 °C | 3340 - 5660 psi @Temperature 140 - 248 °F | Average value: 30.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 35.0 - 121 MPa | 5080 - 17500 psi | Average value: 78.8 MPa Grade Count:22 |
| Elongation at Break | 0.500 - 155 % | 0.500 - 155 % | Average value: 10.3 % Grade Count:82 |
| Elongation at Yield | 2.70 - 15.0 % | 2.70 - 15.0 % | Average value: 7.59 % Grade Count:12 |
| Modulus of Elasticity | 1.35 - 8.96 GPa | 196 - 1300 ksi | Average value: 4.09 GPa Grade Count:70 |
| Flexural Yield Strength | 10.3 - 230 MPa | 1500 - 33400 psi | Average value: 122 MPa Grade Count:59 |
| Flexural Modulus | 2.10 - 8.62 GPa | 305 - 1250 ksi | Average value: 4.46 GPa Grade Count:69 |
| 0.900 - 1.95 GPa @Temperature 60.0 - 120 °C | 131 - 283 ksi @Temperature 140 - 248 °F | Average value: 1.40 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.160 - 1.28 J/cm | 0.300 - 2.40 ft-lb/in | Average value: 0.504 J/cm Grade Count:28 |
| 0.400 - 0.400 J/cm @Temperature -40.0 - -20.0 °C | 0.749 - 0.749 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.400 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.33 J/cm - NB | 2.50 ft-lb/in - NB | Average value: 5.25 J/cm Grade Count:21 |
| Izod Impact, Notched (ISO) | 2.50 - 12.0 kJ/m² | 1.19 - 5.71 ft-lb/in² | Average value: 5.37 kJ/m² Grade Count:25 |
| 2.00 - 42.0 kJ/m² @Temperature -40.0 - -30.0 °C | 0.952 - 20.0 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 10.8 kJ/m² Grade Count:8 | |
| Izod Impact, Unnotched (ISO) | 15.0 - 80.0 kJ/m² | 7.14 - 38.1 ft-lb/in² | Average value: 36.9 kJ/m² Grade Count:12 |
| 25.0 - 40.0 kJ/m² @Temperature -30.0 - -30.0 °C | 11.9 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 34.7 kJ/m² Grade Count:5 | |
| Charpy Impact Unnotched | 1.50 J/cm² - NB | 7.14 ft-lb/in² - NB | Average value: 4.97 J/cm² Grade Count:50 |
| 1.20 - 9.00 J/cm² @Temperature -40.0 - 30.0 °C | 5.71 - 42.8 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 4.03 J/cm² Grade Count:23 | |
| Charpy Impact, Notched | 0.200 - 1.80 J/cm² | 0.952 - 8.57 ft-lb/in² | Average value: 0.698 J/cm² Grade Count:48 |
| 0.100 - 1.00 J/cm² @Temperature -40.0 - 30.0 °C | 0.476 - 4.76 ft-lb/in² @Temperature -40.0 - 86.0 °F | Average value: 0.489 J/cm² Grade Count:20 | |
| Puncture Energy | 1.70 - 1.70 J @Temperature -30.0 - -30.0 °C | 1.25 - 1.25 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.70 J Grade Count:2 |
| 1.70 - 1.70 J @Load <=70.4 kg | 1.25 - 1.25 ft-lb @Load <=155 lb | Average value: 1.70 J Grade Count:2 | |
| Tensile Creep Modulus, 1000 hours | 2000 MPa | 290000 psi | Average value: 2000 MPa Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+10 - 1.00e+15 ohm-cm | 1.00e+10 - 1.00e+15 ohm-cm | Average value: 4.68e+14 ohm-cm Grade Count:47 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 7.71e+14 ohm Grade Count:30 |
| Dielectric Constant | 2.60 - 6.00 | 2.60 - 6.00 | Average value: 4.55 Grade Count:25 |
| Dielectric Strength | 15.7 - 80.0 kV/mm | 400 - 2030 kV/in | Average value: 32.9 kV/mm Grade Count:36 |
| Dissipation Factor | 0.0180 - 0.0700 | 0.0180 - 0.0700 | Average value: 0.0371 Grade Count:7 |
| Dielectric Loss Index | 0.0200 - 0.200 | 0.0200 - 0.200 | Average value: 0.110 Grade Count:16 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 463 V Grade Count:29 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.350 - 90.0 µm/m-°C | 0.194 - 50.0 µin/in-°F | Average value: 45.8 µm/m-°C Grade Count:33 |
| CTE, linear, Transverse to Flow | 70.0 - 97.0 µm/m-°C | 38.9 - 53.9 µin/in-°F | Average value: 84.9 µm/m-°C Grade Count:11 |
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | Average value: 1.40 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.340 - 0.360 W/m-K | 2.36 - 2.50 BTU-in/hr-ft²-°F | Average value: 0.344 W/m-K Grade Count:5 |
| Melting Point | 205 - 255 °C | 401 - 491 °F | Average value: 219 °C Grade Count:57 |
| Maximum Service Temperature, Air | 80.0 - 200 °C | 176 - 392 °F | Average value: 143 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 - 218 °C | 338 - 424 °F | Average value: 197 °C Grade Count:45 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 230 °C | 122 - 446 °F | Average value: 126 °C Grade Count:75 |
| Vicat Softening Point | 190 - 247 °C | 374 - 477 °F | Average value: 204 °C Grade Count:29 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:61 |
| Oxygen Index | 24.0 - 31.0 % | 24.0 - 31.0 % | Average value: 27.3 % Grade Count:4 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 686 °C Grade Count:17 |
| Shrinkage | 0.200 - 0.300 % @Temperature 120 - 120 °C | 0.200 - 0.300 % @Temperature 248 - 248 °F | Average value: 0.250 % Grade Count:1 |
| 0.200 - 0.300 % @Time 14400 - 14400 sec | 0.200 - 0.300 % @Time 4.00 - 4.00 hour | Average value: 0.250 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 271 °C | 176 - 520 °F | Average value: 230 °C Grade Count:15 |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Average value: 70.0 °C Grade Count:4 |
| Nozzle Temperature | 210 - 277 °C | 410 - 530 °F | Average value: 250 °C Grade Count:3 |
| Melt Temperature | 220 - 302 °C | 428 - 576 °F | Average value: 265 °C Grade Count:51 |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | Average value: 77.5 °C Grade Count:60 |
| Drying Temperature | 75.0 - 100 °C | 167 - 212 °F | Average value: 81.8 °C Grade Count:35 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.41 hour Grade Count:28 |
| Moisture Content | 0.0300 - 1.80 % | 0.0300 - 1.80 % | Average value: 0.200 % Grade Count:28 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | Average value: 90.0 MPa Grade Count:25 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:3 |
| Screw Speed | 30.0 - 200 rpm | 30.0 - 200 rpm | Average value: 91.7 rpm Grade Count:3 |