- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.3
- 拉伸强度 [MPa]: 29.0
- 断裂伸长率 [%]: 28.0
- 弯曲强度 [MPa]: 79.3
- 弯曲模量 [MPa]: 0.520
- 硬度: 97.0
- 热变形温度 [℃]: 81.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.29 g/cc | 0.0372 - 0.0466 lb/in³ | Average value: 1.13 g/cc Grade Count:51 |
| Water Absorption | 0.0200 - 10.0 % | 0.0200 - 10.0 % | Average value: 2.00 % Grade Count:36 |
| Moisture Absorption at Equilibrium | 1.30 - 3.00 % | 1.30 - 3.00 % | Average value: 2.63 % Grade Count:26 |
| Water Absorption at Saturation | 8.50 - 10.0 % | 8.50 - 10.0 % | Average value: 9.41 % Grade Count:23 |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | Average value: 40.3 cc/m²/day Grade Count:17 |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | Average value: 14.0 cc-mm/m²-24hr-atm Grade Count:17 |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | Average value: 72.8 cc-mm/m²-24hr-atm Grade Count:17 |
| Viscosity Measurement | 3.00 - 205 | 3.00 - 205 | Average value: 74.9 Grade Count:18 |
| Maximum Moisture Content | 0.0800 | 0.0800 | Average value: 0.0800 Grade Count:17 |
| Linear Mold Shrinkage | 0.00130 - 0.0170 cm/cm | 0.00130 - 0.0170 in/in | Average value: 0.0103 cm/cm Grade Count:14 |
| Linear Mold Shrinkage, Transverse | 0.00110 - 0.00140 cm/cm | 0.00110 - 0.00140 in/in | Average value: 0.00125 cm/cm Grade Count:4 |
| Melt Flow | 1.10 - 9.00 g/10 min | 1.10 - 9.00 g/10 min | Average value: 2.52 g/10 min Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 | 85.0 | Average value: 85.0 Grade Count:3 |
| Hardness, Rockwell R | 97.0 - 119 | 97.0 - 119 | Average value: 108 Grade Count:6 |
| Ball Indentation Hardness | 50.0 - 160 MPa | 7250 - 23200 psi | Average value: 132 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 79.3 - 80.0 MPa | 11500 - 11600 psi | Average value: 79.8 MPa Grade Count:3 |
| Tensile Strength, Yield | 29.0 - 186 MPa | 4210 - 27000 psi | Average value: 70.6 MPa Grade Count:33 |
| Elongation at Break | 1.50 - 315 % | 1.50 - 315 % | Average value: 110 % Grade Count:29 |
| Elongation at Yield | 3.40 - 92.0 % | 3.40 - 92.0 % | Average value: 15.9 % Grade Count:8 |
| Modulus of Elasticity | 0.350 - 3.50 GPa | 50.8 - 508 ksi | Average value: 2.23 GPa Grade Count:14 |
| Flexural Yield Strength | 28.0 - 276 MPa | 4060 - 40000 psi | Average value: 94.5 MPa Grade Count:23 |
| Flexural Modulus | 0.520 - 13.8 GPa | 75.4 - 2000 ksi | Average value: 3.06 GPa Grade Count:16 |
| Izod Impact, Notched | 0.300 - 5.30 J/cm | 0.562 - 9.93 ft-lb/in | Average value: 1.33 J/cm Grade Count:21 |
| Izod Impact, Notched (ISO) | 8.00 - 100000 kJ/m² | 3.81 - 47600 ft-lb/in² | Average value: 8.00 kJ/m² Grade Count:4 |
| Charpy Impact Unnotched | 12.5 J/cm² - NB | 59.5 ft-lb/in² - NB | Average value: 16.2 J/cm² Grade Count:8 |
| 999.9 - 999.9 J/cm² @Temperature -30.0 - -30.0 °C | 4759 - 4759 ft-lb/in² @Temperature -22.0 - -22.0 °F | Grade Count:2 | |
| Charpy Impact, Notched | 0.550 - 11.0 J/cm² | 2.62 - 52.4 ft-lb/in² | Average value: 3.67 J/cm² Grade Count:6 |
| 6.00 - 7.00 J/cm² @Temperature -30.0 - -30.0 °C | 28.6 - 33.3 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.75 J/cm² Grade Count:2 | |
| Coefficient of Friction | 0.0400 - 0.600 | 0.0400 - 0.600 | Average value: 0.284 Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+15 ohm-cm | 1.00e+12 - 1.00e+15 ohm-cm | Average value: 4.08e+14 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 2.04e+14 ohm Grade Count:10 |
| Dielectric Constant | 2.50 - 20.0 | 2.50 - 20.0 | Average value: 4.81 Grade Count:9 |
| Dielectric Strength | 13.0 - 100 kV/mm | 330 - 2540 kV/in | Average value: 30.8 kV/mm Grade Count:16 |
| Dissipation Factor | 0.0190 - 0.0620 | 0.0190 - 0.0620 | Average value: 0.0266 Grade Count:4 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 170 µm/m-°C | 11.0 - 94.4 µin/in-°F | Average value: 86.9 µm/m-°C Grade Count:16 |
| CTE, linear, Transverse to Flow | 90.0 - 190 µm/m-°C | 50.0 - 106 µin/in-°F | Average value: 130 µm/m-°C Grade Count:4 |
| Thermal Conductivity | 0.230 - 0.280 W/m-K | 1.60 - 1.94 BTU-in/hr-ft²-°F | Average value: 0.263 W/m-K Grade Count:6 |
| Melting Point | 210 - 222 °C | 410 - 432 °F | Average value: 220 °C Grade Count:34 |
| Maximum Service Temperature, Air | 70.0 - 160 °C | 158 - 320 °F | Average value: 118 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 - 216 °C | 178 - 420 °F | Average value: 167 °C Grade Count:23 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 204 °C | 122 - 400 °F | Average value: 75.7 °C Grade Count:31 |
| Vicat Softening Point | 129 - 200 °C | 264 - 392 °F | Average value: 176 °C Grade Count:3 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:15 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 - 295 °C | 450 - 563 °F | Average value: 261 °C Grade Count:11 |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | Average value: 251 °C Grade Count:3 |
| Adapter Temperature | 260 - 266 °C | 500 - 511 °F | Average value: 262 °C Grade Count:17 |
| Die Temperature | 254 - 260 °C | 490 - 500 °F | Average value: 257 °C Grade Count:17 |
| Melt Temperature | 138 - 300 °C | 280 - 572 °F | Average value: 252 °C Grade Count:21 |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | Average value: 64.8 °C Grade Count:3 |
| Drying Temperature | 76.0 - 100 °C | 169 - 212 °F | Average value: 82.6 °C Grade Count:4 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.00 hour Grade Count:3 |
| Moisture Content | 0.0400 - 0.0800 % | 0.0400 - 0.0800 % | Average value: 0.0621 % Grade Count:14 |