- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.9
- 断裂伸长率 [%]: 350
- 弯曲强度 [MPa]: 230.0
- 弯曲模量 [MPa]: 11.2
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO data |
| Water Absorption | 0.90 % | 0.90 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.2 % | 5.2 % | in water; 23°C; ISO data |
| Viscosity Measurement | 50 | 50 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 230 MPa | 33400 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 2.0 % | 2.0 % | Strain at break, ISO, 5 mm/min |
| 2.0 % | 2.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 13.5 GPa | 1960 ksi | ASTM test |
| 13.54 GPa | 1964 ksi | ISO test | |
| Flexural Yield Strength | 350 MPa | 50800 psi | ASTM Data |
| Flexural Modulus | 11.2 GPa | 1620 ksi | ISO Value |
| 11.7 GPa | 1700 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 5.00 GPa | 725 ksi | calculated |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 20.0 °C | 17.8 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 79.0 µm/m-°C @Temperature 20.0 °C | 43.9 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ISO data |
| 212 °C | 414 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |