- 密度 [g/cm3]: 1.23
- 拉伸强度 [MPa]: 70.0
- 断裂伸长率 [%]: 100
- 弯曲强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 2.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM value at 50 mm/min. |
| 72.0 MPa | 10400 psi | ISO value at 50 mm/min. | |
| Elongation at Break | 8.5 % | 8.5 % | Nominal strain at break, ISO, 50 mm/min |
| 9.0 % | 9.0 % | Strain at break, ASTM, 5 mm/min | |
| Elongation at Yield | 5.6 % | 5.6 % | ISO Value at 50 mm/min. |
| 6.0 % | 6.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 2.69 GPa | 390 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 100 MPa | 14500 psi | ASTM Data |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM Data |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 400 V | 400 V | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |