- 密度 [g/cm3]: 1.13
- 拉伸强度 [MPa]: 45.0
- 断裂伸长率 [%]: 40.0
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 0.970
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM value at 50 mm/min. |
| 49.0 MPa | 7110 psi | ISO value at 50 mm/min. | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO data, 50 mm/min |
| >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 15 % | 15 % | ASTM Value at 50 mm/min. |
| 22 % | 22 % | ISO Value at 50 mm/min. | |
| Tensile Modulus | 1.36 GPa | 197 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 40.0 MPa | 5800 psi | ASTM Data |
| Flexural Modulus | 0.970 GPa | 141 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 °C | 500 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |