- 密度 [g/cm3]: 1.32
- 断裂伸长率 [%]: 140
- 弯曲强度 [MPa]: 105.0
- 弯曲模量 [MPa]: 3.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | ASTM data at 5 mm/min. |
| Flexural Yield Strength | 140 MPa | 20300 psi | ASTM Data |
| Flexural Modulus | 3.86 GPa | 560 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |