- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 1.2
- 断裂伸长率 [%]: 150
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 4.14
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO data |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.0 % | 7.0 % | in water; 23°C; ISO data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ASTM data at 5 mm/min. |
| 92.0 MPa | 13300 psi | ISO value at 5mm/min. | |
| Flexural Yield Strength | 150 MPa | 21800 psi | ASTM Data |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |