- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.8
- 断裂伸长率 [%]: 260
- 弯曲强度 [MPa]: 190.0
- 弯曲模量 [MPa]: 9.20
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO data |
| Water Absorption | 0.80 % | 0.80 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 4.8 % | 4.8 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO data |
| 0.0020 cm/cm | 0.0020 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 2.5 % | 2.5 % | Strain at break, ASTM, 5 mm/min |
| 2.6 % | 2.6 % | Strain at break, ISO, 5 mm/min | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 260 MPa | 37700 psi | ASTM Data |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO Value |
| 10.345 GPa | 1500.4 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 4.40 GPa | 638 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 20.0 °C | 10.6 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature 20.0 °C | 41.1 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO data |
| 210 °C | 410 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |