- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 1.1
- 断裂伸长率 [%]: 210
- 弯曲强度 [MPa]: 138.0
- 弯曲模量 [MPa]: 2.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.3 % | 6.3 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ISO data |
| Elongation at Break | 4.0 % | 4.0 % | Strain at break, ISO, 5 mm/min |
| Tensile Modulus | 7.41 GPa | 1070 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 210 MPa | 30500 psi | ASTM Data |
| Flexural Modulus | 2.90 GPa | 421 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 2.70 GPa | 392 ksi | calculated |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO data |
| 210 °C | 410 °F | ASTM Data | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |