- 密度 [g/cm3]: 1.43
- 拉伸强度 [MPa]: 50.0
- 断裂伸长率 [%]: 70.0
- 弯曲模量 [MPa]: 2.14
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM test; 50 mm/min. |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ASTM, 50 mm/min |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM Data |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |