- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 1.1
- 弯曲强度 [MPa]: 99.0
- 弯曲模量 [MPa]: 5.20
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.4 % | 6.4 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 99.0 MPa | 14400 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 99.0 MPa | 14400 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 7.0 % | 7.0 % | 5mm/min; ISO 527 | ||
| 7.0 % | 7.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.60 GPa | 812 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO Data | ||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO Data | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||