- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 1.1
- 缺口冲击强度: 8.5
- 弯曲强度 [MPa]: 155.0
- 弯曲模量 [MPa]: 8.70
- 硬度: 121.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.4 % | 6.4 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 160 MPa | 23200 psi | 0.2 in/min; ASTM Test | ||
| 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | ISO Data | |||
| 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | ASTM Test | |||
| 85.0 MPa @Temperature 80.0 °C | 12300 psi @Temperature 176 °F | ASTM Test | |||
| 85.0 MPa @Temperature 80.0 °C | 12300 psi @Temperature 176 °F | ISO Data | |||
| 210 MPa @Temperature -40.0 °C | 30500 psi @Temperature -40.0 °F | ISO Data | |||
| 210 MPa @Temperature -40.0 °C | 30500 psi @Temperature -40.0 °F | ASTM Test | |||
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ISO Data | |||
| 7.0 % @Temperature 80.0 °C | 7.0 % @Temperature 176 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ASTM Test | |||
| 7.0 % @Temperature 80.0 °C | 7.0 % @Temperature 176 °F | ASTM Test | |||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1mm/min; ISO 527 | ||
| 4.015 GPa @Temperature 120 °C | 582.3 ksi @Temperature 248 °F | ISO Data | |||
| 4.66 GPa @Temperature 80.0 °C | 676 ksi @Temperature 176 °F | ISO Data | |||
| 10.4 GPa @Temperature -40.0 °C | 1510 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 225 MPa | 32600 psi | ISO Data | ||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO Test | ||
| 6.00 kJ/m² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 | ||
| 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 208 °C | 406 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-106 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||