- 密度 [g/cm3]: 1.067
- 吸水率 [%]: 1.4
- 弯曲强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.21
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.067 g/cc | 0.03855 lb/in³ | Melt; ISO 1183 | ||
| 1.23 g/cc | 0.0444 lb/in³ | dry; ISO 1183 | |||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 0.2 in/min; ASTM Test | ||
| 20.0 MPa @Temperature 80.0 °C | 2900 psi @Temperature 176 °F | ISO Data | |||
| 20.0 MPa @Temperature 80.0 °C | 2900 psi @Temperature 176 °F | ASTM Test | |||
| 40.0 MPa @Temperature 120 °C | 5800 psi @Temperature 248 °F | ISO Data | |||
| 40.0 MPa @Temperature 120 °C | 5800 psi @Temperature 248 °F | ASTM Test | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM Test | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 9.0 % | 9.0 % | 5mm/min; ISO 527 | ||
| 9.0 % | 9.0 % | 0.2 in/min; ASTM Test | |||
| 4.0 % @Temperature -40.0 °C | 4.0 % @Temperature -40.0 °F | ASTM Test | |||
| 4.0 % @Temperature -40.0 °C | 4.0 % @Temperature -40.0 °F | ISO Data | |||
| 6.0 % @Temperature 120 °C | 6.0 % @Temperature 248 °F | ISO Data | |||
| 6.0 % @Temperature 120 °C | 6.0 % @Temperature 248 °F | ASTM Test | |||
| 15 % @Temperature 80.0 °C | 15 % @Temperature 176 °F | ASTM Test | |||
| 15 % @Temperature 80.0 °C | 15 % @Temperature 176 °F | ISO Data | |||
| Tensile Modulus | 2.64 GPa | 383 ksi | 1mm/min; ISO 527 | ||
| 1.90 GPa @Temperature 120 °C | 276 ksi @Temperature 248 °F | ISO Data | |||
| 2.30 GPa @Temperature 80.0 °C | 334 ksi @Temperature 176 °F | ISO Data | |||
| 6.60 GPa @Temperature -40.0 °C | 957 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 65.0 MPa | 9430 psi | ISO Data | ||
| 101 MPa | 14600 psi | ASTM Test | |||
| 219 MPa @Temperature -40.0 °C | 31800 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 2.21 GPa | 321 ksi | ISO Data | ||
| 2.40 GPa | 348 ksi | ASTM Test | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.728 J/g-°C | 0.6520 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||