- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 1.1
- 缺口冲击强度: 1.1
- 弯曲强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 8.50
- 硬度: 121.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.4 % | 6.4 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 0.2 in/min; ASTM Test | ||
| 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | ASTM Test | |||
| 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | ISO Data | |||
| 90.0 MPa @Temperature 80.0 °C | 13100 psi @Temperature 176 °F | ISO Data | |||
| 90.0 MPa @Temperature 80.0 °C | 13100 psi @Temperature 176 °F | ASTM Test | |||
| 230 MPa @Temperature -40.0 °C | 33400 psi @Temperature -40.0 °F | ASTM Test | |||
| 230 MPa @Temperature -40.0 °C | 33400 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 10.2 GPa | 1480 ksi | 1mm/min; ISO 527 | ||
| 4.01 GPa @Temperature 120 °C | 582 ksi @Temperature 248 °F | ISO Data | |||
| 4.82 GPa @Temperature 80.0 °C | 699 ksi @Temperature 176 °F | ISO Data | |||
| 10.3 GPa @Temperature -40.0 °C | 1490 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 245 MPa | 35500 psi | ISO Data | ||
| 280 MPa | 40600 psi | ASTM Test | |||
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO Data | ||
| 8.99 GPa | 1300 ksi | ASTM Test | |||
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.17 mm | 2.06 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| 218 °C | 424 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 208 °C | 406 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||