- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 84.0
- 弯曲模量 [MPa]: 0.310
- 硬度: 99.0
- 热变形温度 [℃]: 169.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.2 % | 9.2 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 220 | 220 | Formic Acid | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 99 | 99 | ASTM Test | ||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 50mm/min; ISO 527 | ||
| 84.0 MPa | 12200 psi | 2 in/min; ASTM Test | |||
| 24.0 MPa @Temperature 120 °C | 3480 psi @Temperature 248 °F | ISO Data | |||
| 24.0 MPa @Temperature 120 °C | 3480 psi @Temperature 248 °F | ASTM Test | |||
| 138 MPa @Temperature -40.0 °C | 20000 psi @Temperature -40.0 °F | ASTM Test | |||
| 138 MPa @Temperature -40.0 °C | 20000 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 100 % | >= 100 % | 2 in/min; ASTM Test | ||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM Test | |||
| Flexural Strength | 114 MPa | 16500 psi | ASTM Test | ||
| 17.0 MPa @Temperature 120 °C | 2470 psi @Temperature 248 °F | ASTM Test | |||
| 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | ASTM Test | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM Test | |||
| 179 MPa @Temperature -40.0 °C | 26000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.310 GPa | 45.0 ksi | |||
| 2.90 GPa | 421 ksi | ASTM Test | |||
| 0.260 GPa @Temperature 120 °C | 37.7 ksi @Temperature 248 °F | ASTM Test | |||
| 0.435 GPa @Temperature 65.0 °C | 63.1 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C | 0.993 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 135 µm/m-°C @Temperature -30.0 - 30.0 °C | 75.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C | 336 °F | ASTM Test | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM Test | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Blow Molding | ||||
| Processing | Blow molding | ||||
| Injection Molding | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||