- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 1.1
- 缺口冲击强度: 6.0
- 弯曲强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 5.20
- 硬度: 119.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 0.2 in/min; ASTM Test | ||
| 30.0 MPa @Temperature 120 °C | 4350 psi @Temperature 248 °F | ISO Data | |||
| 30.0 MPa @Temperature 120 °C | 4350 psi @Temperature 248 °F | ASTM Test | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ASTM Test | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ISO Data | |||
| 135 MPa @Temperature -40.0 °C | 19600 psi @Temperature -40.0 °F | ASTM Test | |||
| 135 MPa @Temperature -40.0 °C | 19600 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 0.2 in/min; ASTM Test | ||
| 10 % | 10 % | 5mm/min; ISO 527 | |||
| 6.0 % @Temperature -40.0 °C | 6.0 % @Temperature -40.0 °F | ISO Data | |||
| 6.0 % @Temperature -40.0 °C | 6.0 % @Temperature -40.0 °F | ASTM Test | |||
| 35 % @Temperature 80.0 °C | 35 % @Temperature 176 °F | ASTM Test | |||
| 35 % @Temperature 80.0 °C | 35 % @Temperature 176 °F | ISO Data | |||
| 40 % @Temperature 120 °C | 40 % @Temperature 248 °F | ASTM Test | |||
| 40 % @Temperature 120 °C | 40 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527 | ||
| 0.970 GPa @Temperature 120 °C | 141 ksi @Temperature 248 °F | ISO Data | |||
| 1.36 GPa @Temperature 80.0 °C | 197 ksi @Temperature 176 °F | ISO Data | |||
| 8.31 GPa @Temperature -40.0 °C | 1210 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 140 MPa | 20300 psi | ISO Data | ||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 13.0 J/cm² | 61.9 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75 | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| X | |||||
| UL.UL-C | Yes | ||||